牌号简介 About |
---|
用于软包装的高性能吹塑薄膜树脂具有优异的耐滥用性、低温密封启动性、优异的光学性能、优异的氧气传输率,符合:美国FDA FCN 424加拿大HPFP无异议欧盟、美国FDA-DMF第10/2011号有关详细信息,请参阅相关法规。亲和力*PF 1140G聚烯烃塑性体(POP)是通过InSite*技术生产的。它是一种乙烯-α-烯烃树脂,设计用于各种苛刻的应用,包括填表密封包装和新鲜产品袋。该树脂与其他聚烯烃具有良好的相容性,允许有效的共混和共挤出。 High performance blown film resin for flexible packaging Excellent abuse resistance Low temperature seal initiation Excellent optics Outstanding high oxygen transmission rates Complies with: U.S. FDA FCN 424 Canadian HPFP No Objections EU, No 10/2011 U.S. FDA-DMF Consult the regulations for complete details. AFFINITY* PF 1140G Polyolefin Plastomer (POP) is produced via INSITE* Technology. It is an ethylene alpha-olefin resin designed to be used in a variety of demanding applications including form-fill-seal packaging and fresh produce bags. This resin has excellent compatibility with other polyolefins, allowing efficient blending and coextrusion. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.897 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
1.6 | g/10min | ASTM D1238 |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
51 | µm | |
膜刺穿强度 Membrane puncture strength |
|||
51 µm 51 µm |
8.18 | J | 内部方法 |
膜刺穿力 Membrane puncture force |
|||
51 µm 51 µm |
83.6 | N | 内部方法 |
膜耐刺穿性 Membrane puncture resistance |
|||
51 µm 51 µm |
J/cm³ | 内部方法 | |
割线模量 Secant modulus |
ASTM D882 | ||
2% 正割,MD:51 µm 2% secant, MD: 51 µ m |
MPa | ||
2% 正割,TD:51 µm 2% secant, TD: 51 µ m |
MPa | ||
拉伸强度 tensile strength |
ASTM D882 | ||
MD,屈服,51 µm MD, yield, 51 µ m |
MPa | ||
TD,屈服,51 µm TD, yield, 51 µ m |
MPa | ||
MD,断裂,51 µm MD, fracture, 51 µ m |
MPa | ||
TD,断裂,51 µm TD, fracture, 51 µ m |
MPa | ||
拉伸应变 Tensile strain |
ASTM D882 | ||
MD,断裂,51 µm MD, fracture, 51 µ m |
% | ||
TD,断裂,51 µm TD, fracture, 51 µ m |
% | ||
落锤冲击 Drop hammer impact |
|||
51 µm 51 µm |
g | ASTM D1709-B | |
埃尔曼多夫抗撕强度 Elmandorf tear strength 1 |
ASTM D1922 | ||
MD:51 µm MD:51 µm |
g | ||
TD:51 µm TD:51 µm |
g | ||
始封温度 Initial sealing temperature 2 |
|||
51 µm 51 µm 2 |
℃ | 内部方法 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 | |
熔融温度 Melting temperature |
|||
DSC DSC |
℃ | 内部方法 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
|||
20°,50.8 µm 20°,50.8 µm |
ASTM D2457 | ||
透明度 transparency |
|||
50.8 µm 50.8 µm |
ASTM D1746 | ||
雾度 Haze |
|||
50.8 µm 50.8 µm |
% | ASTM D1003 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 改性过的矩形测件。 |
3 实现 2 磅/英寸 (8.8 N/25.4 mm) 热封强度的温度。 热封强度,Topwave HT 测试仪 0.5 S 保压,40 psi 压力,拉动速度 10 英寸/分(250 mm/秒)。 |
【新闻资讯】查看全部
化销华南汽运乙烯业务实现零的突破
2022-01-21 搜料网资讯: 1月16日18时,中科炼化首车乙烯顺利装车出厂,标志着化销华南首次打通乙烯公路运输流程,填补了华南地区汽运乙烯的业务空白,为中科炼化乙烯产品后路畅通提供了有 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |