牌号简介 About |
---|
Solanyl® C8103是一种适用于薄膜应用的端部化合物,专门用于包装。Solanyl® C8103可在适合(多层)柔性薄膜的传统吹塑或铸膜挤出生产线上加工。Solanyl® C8103是目前广泛应用的生物塑料和低密度聚乙烯的竞争替代品。Solanyl® C8103具有自然的感觉和外观,可生物降解,植物源性含量大于40%,生物基碳含量约为30%。Solanyl® C8103可用于:(快餐)包装和消费品运输和垃圾袋一次性可处置农业产品的短寿命可生物降解产品。 Solanyl® C8103 is an end compound suitable for film applications and is specially developed for packaging. Solanyl® C8103 can be processed on conventional blown or cast film extrusion lines suitable for (multi-layer) flexible films. Solanyl® C8103 is a ompetitive alternative for currently used bioplastics and LDPE for a wide range of applications. Solanyl® C8103 has a natural feel and look, is biodegradable and has a plant derived content of >40% with biobased carbon at ~30%. Applications in which Solanyl® C8103 can be used are: (Fast food) Packaging & Consumer goods Carrier & refuse bags Short life biodegradable products for single use disposables Agriculture products |
技术参数 Technical Data | |||
---|---|---|---|
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
25 | µm | |
拉伸模量 Tensile modulus |
|||
MD MD |
< 200 | MPa | |
TD TD |
< 200 | MPa | |
拉伸强度 tensile strength |
|||
MD,屈服 MD, yield |
8.00 到 11.0 | MPa | |
TD,屈服 TD, yield |
7.00 到 10.0 | MPa | |
MD MD |
MPa | ||
TD TD |
MPa | ||
拉伸应变 Tensile strain |
|||
MD,屈服 MD, yield |
% | ||
TD,屈服 TD, yield |
% | ||
MD,断裂 MD, fracture |
% | ||
TD,断裂 TD, fracture |
% | ||
落锤冲击 Drop hammer impact |
g | ASTM D1709 | |
埃尔曼多夫抗撕强度 Elmandorf tear strength |
|||
MD MD |
N | ||
TD TD |
N | ||
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
|||
注塑成型 injection molding |
ISO 179/1eU | ||
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
|||
注塑 Injection molding |
ISO 180/1U | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
玻璃化转变温度 Glass transition temperature |
℃ | DSC | |
维卡软化温度 Vicat Softening Temp |
℃ | ISO 306/A | |
熔融温度 Melting temperature |
|||
DSC DSC |
℃ | 内部方法 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
Water Activity Water Activity |
内部方法 | ||
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
g/cm³ | ISO 1183 | |
表观密度 Apparent density |
g/cm³ | ISO 60 | |
熔体质量流动速率 Melt Flow Rate |
|||
170℃,2.16kg 170℃,2.16kg |
g/10min | ||
190℃,5.0kg 190℃,5.0kg |
g/10min | ISO 1133 | |
收缩率 Shrinkage rate |
% | ISO 294-4 | |
含水量 water content |
内部方法 | ||
颗粒大小 Particle size |
mm | 内部方法 | |
熔体密度 Melt density |
g/cm³ | ISO 1133 |
备注 | |||
---|---|---|---|
暂无数据 |
【新闻资讯】查看全部
中欧宣布完成投资协定谈判
2021-01-03 搜料网资讯: 展现中国对外开放决心 据俄罗斯卫星社12月30日援引新华社报道,中国国家主席习近平表示,中欧达成投资协定展现了中方推进高水平对外开放的决心和信心。他强调,中 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |