牌号简介 About |
---|
Monosol AF L711是一种基于聚乙烯醇的热塑性薄膜,可溶于冷水,使用Monosol AF的专有吹塑薄膜技术制造。Monosol AF L711是一种聚乙烯醇冷水溶性薄膜,设计用于片剂的流动包装和褶皱包装。该薄膜具有良好的硬度,便于在流动包装和褶皱包装设备上加工。可用厚度范围为20微米(0.8密耳)至60微米(2.4密耳)。 MonoSol AF L711 is a PVOH based thermoplastic film, soluble in cold water and manufactured using MonoSol AF's proprietary blown film technology. MonoSol AF L711 is a grade of PVOH cold water-soluble film engineered for flow wrapping and pleat wrapping of tablets. This film has excellent stiffness for ease of processing on flow wrapping and pleat wrapping equipment. Available thickness range is 20 micron (0.8 mil) to 60 micron (2.4 mil). |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
含水量 water content 2 |
|||
23℃ 23℃ 2 |
7.0 | % | |
可溶性 solubility 3 |
|||
Disintegration:24℃,20.1 µm Disintegration:24℃,20.1 µm |
3.0 | sec | |
Dissolution:24℃,20.1 µm Dissolution:24℃,20.1 µm |
41.0 | sec | |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
20 | µm | |
割线模量 Secant modulus |
|||
10%,MD:20 µm 10%,MD:20 µm |
186 | MPa | |
10%,TD:20 µm 10%,TD:20 µm |
MPa | ||
拉伸强度 tensile strength |
|||
MD,断裂,20 µm MD, fracture, 20 µ m |
MPa | ASTM D882 | |
TD,断裂,20 µm TD, fracture, 20 µ m |
MPa | ASTM D882 | |
MD,20 µm MD,20 µm |
MPa | ISO 527-3 | |
TD,20 µm TD,20 µm |
MPa | ISO 527-3 | |
拉伸应变 Tensile strain |
|||
MD,断裂,20 µm MD, fracture, 20 µ m |
% | ||
TD,断裂,20 µm TD, fracture, 20 µ m |
% | ||
用量 dosage |
|||
density at 1.25 g/cc,20.0 µm density at 1.25 g/cc,20.0 µm |
m²/kg |
备注 |
---|
2、50%RH |
3、Distilled Water (MSTM 205) |
【新闻资讯】查看全部
高耐用热塑性塑料泡沫及复合资料处理风力叶片回收难题
2017-06-20 据悉,Fraunhofer的研究人员与行业专家合作开发的高耐用热塑性塑料泡沫及复合材料,不仅减轻了叶片的重量而且使其可以回收利用,解决了其运输、组装、拆卸和处理的难题。 由于其特殊性能,新材料也适合汽车等行业的其它轻量级构件。他们的第一个产品将在于10月19日至26日举办的2016年Düsseldorf国际塑料及橡胶博览会上呈现。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |