| 牌号简介 About |
|---|
| 压力管道用中密度湿固化聚乙烯复合材料。适用于高达200°F的Dr 9压力管道应用。Pexidan L/T flex是一种中等密度的PEX系统，由硅烷接枝的碱化合物A-1025和催化剂母料CAT-003组成，比高密度PEX管道材料具有更大的灵活性。当以适当比例混合和挤压时，双组分系统会产生一种材料，该材料可通过暴露于水分或在90-95°C的热水中浸泡而交联。pexidan l/t flex符合NSF国际标准14和ASTM F876非饮用水压力管应用标准。该系统有红色、白色、蓝色和天然色，也可以在挤压时着色。 Medium density moisture-curable PE compound for pressure pipe. Suitable for DR 9 pressure pipe applications operating up to 200°F. PEXIDAN ® L/T Flex is a medium density PEX system consisting of a silane grafted base-compound A-1025 and a catalyst masterbatch CAT-003 and featuring much improved flexibility over high density PEX pipe materials. When mixed and extruded in the proper proportions, the two-component system results in a material that is crosslinkable by exposure to moisture or by immersion in hot water at 90-95°C. PEXIDAN ® L/T Flex meets NSF International Standard 14 and ASTM F876 standard for non-potable water pressure pipe applications. The system is available in red, white, blue and natural, or can be colored at extrusion. |
产品描述 Product Description
用途：管道系统;
加工条件：管路挤出成型
性能特点： 可交联; 韧性好; Good flexibility,Crosslinked
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density 2 |
0.937 | g/cm³ | ASTM D792 |
|
熔体质量流动速率 Melt Flow Rate |
|||
|
190℃，2.16kg 190℃，2.16kg |
0.20 | g/10min | ASTM D1238 |
|
交叉结合的程度 The degree of cross combination |
> 80 | % | ASTM D2765 |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸强度 tensile strength |
|||
|
屈服，23℃ Yield, 23 ℃ |
20.0 | MPa | |
|
断裂，23℃ Fracture, 23 ℃ |
25.5 | MPa | |
|
拉伸应变 Tensile strain |
|||
|
屈服，23℃ Yield, 23 ℃ |
% | ||
|
断裂，23℃ Fracture, 23 ℃ |
% | ||
|
弯曲模量 Bending modulus |
|||
|
2% 正割 2% secant |
MPa | ISO 178 | |
|
流体静力学设计基础 - @ >80% DOC Fundamentals of Hydrostatic Design - @>80% DOC |
|||
|
23℃ 23℃ |
MPa | ||
|
82℃ 82℃ |
MPa | ||
|
93℃ 93℃ |
MPa | ||
|
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
高温伸长率 High temperature elongation 3 |
|||
|
负荷下伸长率：150℃ Elongation under load: 150 ℃ |
% | ||
|
permanent elongation（set） after cooling：150℃ permanent elongation（set） after cooling：150℃ |
% | ||
|
|
|||
| 备注 |
|---|
| 2. 23°C |
| 3. 15 minutes, 0.2 N/mm² load |
|
【新闻资讯】查看全部 
金发科技近日正式发布“碳”战略与行动计划，聚焦回收及再生塑料
2021-10-20 搜料网资讯： 近日，金发科技股份有限公司，正式发布碳战略与行动计划。 金发科技致力于与合作伙伴共同成长、共享成果，为社会提供优质的新材料产品，创造美好生活。为响应国家 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付