牌号简介 About |
---|
Fusabond® M623XF树脂是一种无规乙烯共聚物,含有一种单体,该单体被归类为马来酸酐当量,用于应用。准确的组成被认为是专有信息。应用:Fusabond® M623XF作为改性剂被用于热熔胶配方中,以提高热熔胶的性能。可与乙烯-丙烯酸酯共聚物和乙烯-丙烯酸酯共聚物混溶:最适合用于乙烯-丙烯酸酯共聚物或乙烯-丙烯酸酯共聚物的热熔配方中,以增强和扩大粘合性能。由于它的高流动性和较高的熔点,它也可能给热熔胶配方的加工和处理带来好处。Fusabond® M623XF也可以分散在乳胶形式,或磨成粉末形式,用于其他工艺应用和最终用途。应用范围包括但不限于:粘合剂、聚合物改性、偶联剂、粉末涂料 Fusabond® M623XF resin is a random ethylene copolymer, incorporating a monomer which is classified as being a maleic anhydride equivalent for application uses. The exact composition is considered to be proprietary information. Applications: Fusabond® M623XF is used as a modifier to be included in hot melt formulations for enhancing the performance of hot melt adhesives. It is miscible with EVA and Ethylene acrylic ester copolymers: It is best used when incorporated in hot melt formulations of EVA or Ethylene acrylic ester copolymers for enhancing and expanding adhesion performance. Because of its high fluidity and higher melting point, it may also impart processing and handling benefits for hot melt formulations. Fusabond® M623XF can also be dispersed in latex form, or ground into powder form, for other process applications, and end uses. Applications include but are not limited to: Adhesives, Polymer Modification, Coupling agent, Powder coating |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.940 | g/cm³ | ASTM D792 |
密度 Density |
0.940 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
ASTM D1238 | ||
120℃,2.16kg 120℃,2.16kg |
60 | g/10min | ASTM D1238 |
190℃,2.16kg 190℃,2.16kg |
400 | g/10min | ASTM D1238 |
熔体质量流动速率 Melt Flow Rate |
ISO 1133 | ||
120℃,2.16kg 120℃,2.16kg |
60 | g/10min | ISO 1133 |
190℃,2.16kg 190℃,2.16kg |
g/10min | ISO 1133 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
熔融温度 Melting temperature |
|||
DSC DSC |
|||
-- -- |
℃ | ASTM D3418 | |
-- -- |
℃ | ISO 3146 | |
冰点 - DSC Freezing point - DSC |
|||
-- -- |
℃ | ISO 3146 | |
-- -- |
℃ | ASTM D3418 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
加工温度 Processing temperature |
℃ |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
薄壁注塑件常见缺陷,难倒你了吗?
2021-02-21 搜料网资讯: 缺陷名称 缺陷成因 模具修正 成型改善 缺料 成品的细小部位、角落处无法完全成型 , 因模具加工不到位或是排气不畅 , 成型上由于注射剂量或压力不够等原因 , 设计缺陷 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |