牌号简介 About |
---|
沙特基础工业公司(SABIC)的高密度聚乙烯(HDPE)级产品在受控条件下生产,产品质量高、一致性好、纯度高。SABIC® HDPE PCG300054是一种高密度聚乙烯共聚物注塑级。其分子量分布窄,流动性好,翘曲度低,刚性好,光泽好,成型周期快。SABIC® HDPE PCG300054建议用于医疗包装应用,如注射器、盖子和封口、薄壁物品和医疗设备的其他零件。SABIC® HDPE PCG300054符合欧洲药典(EP)和美国药典(USPVI)的相关专著。本发明所述产品不得用于医疗保健设备或用于人体内临时或永久实施的材料。 SABIC® HDPE grades for healthcare applications are produced under controlled conditions resulting in high product quality, consistency and a high level of purity. SABIC® HDPE PCG300054 is a high density polyethylene copolymer injection moulding grade. Its narrow molecular weight distribution and high flow results in low warpage, good rigidity, excellent gloss and fast moulding cycles. SABIC® HDPE PCG300054 is recommended for healthcare packaging applications like, syringes, caps and closures, thin wall articles and other parts for medical devices. SABIC® HDPE PCG300054 complies with the relevant monographs of the European Pharmacopoeia (EP) and the United States Pharmacopoeia (USPVI). The product mentioned herein may not be used for medical healthcare devices or materials intended for temporary or permanent implementation in the human body. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.954 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
ISO 1133 | ||
190℃,2.16kg 190℃,2.16kg |
30 | g/10min | ISO 1133 |
190℃,5.0kg 190℃,5.0kg |
80 | g/10min | ISO 1133 |
熔体体积流动速率 Melt Volume Rate |
ISO 1133 | ||
190℃,2.16 kg 190℃,2.16 kg |
40.0 | cm³/10min | ISO 1133 |
190℃,5 kg 190℃,5 kg |
105 | cm³/10min | ISO 1133 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ISO 180/A | ||
-30℃,模压成型 -30 ℃, molded |
kJ/m² | ISO 180-A | |
23℃,模压成型 23 ℃, molded |
kJ/m² | ISO 180-A | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
维卡软化温度 Vicat Softening Temp |
℃ | ISO 306/A | |
熔融温度 Melting temperature |
|||
DSC DSC |
℃ | DIN 53765 | |
Enthalpy Change Enthalpy Change |
J/g | DIN 53765 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D,模压成型 Shaw's D, molded |
ISO 868 | ||
拉伸模量 Tensile modulus |
|||
2 mm,模压成型 2 mm, molded into shape |
MPa | ISO 527-2/1BA/50 | |
拉伸强度 tensile strength |
ISO 527-2/1BA/50 | ||
屈服,2 mm,模压成型 Yield, 2 mm, molded |
MPa | ISO 527-2/1BA/50 | |
断裂,2 mm,模压成型 Fracture, 2 mm, molded |
MPa | ISO 527-2/1BA/50 | |
拉伸应变 Tensile strain |
|||
断裂,2 mm,模压成型 Fracture, 2 mm, molded |
% | ISO 527-2/1BA/50 | |
拉伸蠕变模量 Tensile creep modulus |
ISO 899-1 | ||
1 hr 1 hr |
MPa | ISO 899-1 | |
1000 hr 1000 hr |
MPa | ISO 899-1 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
中韩石化30万吨/年聚丙烯项目全力冲刺保开车
2021-03-01 搜料网资讯: 连日来,炼化工程十建公司承建的中韩石化新建30万吨/年聚丙烯项目进入施工扫尾阶段,参建员工春节期间坚守岗位全力冲刺各专业施工节点,确保项目按期实现开车投料 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |