牌号简介 About |
---|
LLC4-020是一种经丁烯共聚单体认证的底漆树脂,设计用于浇铸或吹塑薄膜,用于拉伸粘合和一般用途。LLC4-020具有易加工性、薄膜强度好、热封范围宽等特点。LLC4-020符合FDA法规21CFR 177.1520(c)3.1a。LLC4-020不含滑动和防阻塞。还提供:B=赤脚A=0防滑/高防阻(0/6500)F=全加(1500/6500) LLC4-020 is a Butene-comonomer certified prime resin designed for Cast or Blown film for Stretch-Cling and General Purpose applications. LLC4-020 features easy processability, good film strength and a broad heat sealing range. LLC4-020 complies with FDA regulation 21CFR 177.1520(c) 3.1a. LLC4-020 contains no slip and no antiblock. Also Available in: B = Barefoot A= 0 Slip / High Anti Block (0/6500) F = Full Adds (1500/6500) |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.918 | g/cm³ | ASTM D1505 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
2.0 | g/10min | ASTM D1238 |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
25 | µm | |
割线模量 Secant modulus |
|||
1% 正割,MD,25 µm 1% secant, MD, 25 µ m |
172 | MPa | ASTM D882 |
拉伸强度 tensile strength |
ASTM D882 | ||
MD,屈服,25 µm MD, yield, 25 µ m |
10.0 | MPa | ASTM D882 |
MD,断裂,25 µm MD, fracture, 25 µ m |
MPa | ASTM D882 | |
拉伸应变 Tensile strain |
|||
MD,断裂,25 µm MD, fracture, 25 µ m |
% | ASTM D882 | |
落锤冲击 Drop hammer impact 2 |
|||
25 µm 25 µm 2 |
g | ASTM D1709-A | |
埃尔曼多夫抗撕强度 Elmandorf tear strength |
|||
MD,25 µm MD,25 µm |
g | ASTM D1922 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 F50 |
【新闻资讯】查看全部
近期PTA期现货延续大涨,新高不时
2018-08-13 近期PTA期现货连续大涨,新高不断,行情呈现鼎沸之势,毫无疑问成为近期市场关注度最高的化工品种。对于现阶段快速变化中聚酯产业链,我们主要观点如下:PX强势推动PTA牛市行情作为近油端化工品,PX价格波动通常同步于油价,然而近期PX相对于原油却显著超涨,我们认原因主要有三:1)汇率因素;2)日韩炼厂挺价,中国民营炼化项目投产前多赚利润;3)地炼降低负荷,石脑油价格上涨推升PX。以上三个因素推升了PX价格,从产业链利润变化情况来看,PX单位利润提升在时间上是领先于PTA,幅度上也是优于PTA的 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |