SABIC PP化合物9710是一种填充矿物的冲击改性聚丙烯TPO。这种材料结合了高耐冲击性,耐刮擦性,热稳定性和汽车内部紫外线稳定性。这种材料在低至0摄氏度的温度下具有延展性。IMDS为164207488。 SABIC® PPCOMPOUND 9710 is a mineral filled, impact modified polypropylene TPO. This material combines high impact resistance, scratch resistance, and heat stability with interior automotive UV stability. This material can exhibit ductility at temperatures as low as 0 degrees C. The IMDS is 164207488. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.04 | g/cm³ | ASTM D792 |
密度 Density |
1.04 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
230℃,2.16kg 230℃,2.16kg |
20 | g/10min | ISO 1133 |
收缩率 Shrinkage rate |
Internal Method | ||
TD:23℃,48 hrs TD:23℃,48 hrs |
0.90 | % | 内部方法 |
MD:23℃,48 hrs MD:23℃,48 hrs |
0.50 | % | 内部方法 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
MPa | ISO 527-1-2 | |
拉伸强度 tensile strength |
|||
断裂 fracture |
MPa | ISO 527-2/1A/50 | |
屈服 yield |
MPa | ISO 527-2/50 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ISO 527-2/50 | |
屈服 yield |
% | ISO 527-2/50 | |
弯曲模量 Bending modulus 2 |
|||
64 mm跨距 64 mm span 2 |
MPa | ISO 178 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
ISO 179/1eA | ||
-30℃ -30℃ 3 |
kJ/m² | ISO 179/1eA | |
0℃ 0℃ 4 |
kJ/m² | ISO 179/1eA | |
23℃ 23℃ 4 |
kJ/m² | ISO 179/1eA | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch 3 |
ISO 180/1A | ||
-30℃ -30℃ |
kJ/m² | ISO 180-1A | |
0℃ 0℃ |
kJ/m² | ISO 180-1A | |
23℃ 23℃ |
kJ/m² | ISO 180-1A | |
装有测量仪表的落镖冲击 Dart impact equipped with measuring instruments 5 |
ASTM D3763 | ||
-30℃,Energy at Peak Load -30℃,Energy at Peak Load |
J | ASTM D3763 | |
0℃,Energy at Peak Load 0℃,Energy at Peak Load |
J | ASTM D3763 | |
23℃,Energy at Peak Load 23℃,Energy at Peak Load |
J | ASTM D3763 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature 3 |
|||
1.8 MPa,未退火 1.8 MPa, unannealed 3 |
℃ | ISO 75-2/A | |
0.45 MPa,未退火 0.45 MPa, unannealed 3 |
℃ | ISO 75-2/B | |
维卡软化温度 Vicat Softening Temp |
|||
A50 A50 |
℃ | ISO 306/A50 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
TD:-30~100℃ TD:-30~100℃ |
1/℃ | ISO 11359-2 | |
MD:-30~100℃ MD:-30~100℃ |
1/℃ | ISO 11359-2 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 0.079 in/min |
3 80*10*4mm, Cut |
4 80*10*4 mm, Cut |
5 21.7 ft/sec |
【新闻资讯】查看全部
SONGWON 产业集团发布2021年第1季度财务业绩报告
2021-05-17 搜料网资讯: 5月14日,SONGWON 产业集团今日发布了2021年第1季度(截止到3月31日)的财务业绩审计报告。继2020年末观察到需求激增,特别是亚洲客户的需求激增之后,SONGWON 进入新的财年 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |