NEPOL GB215HP是一种20%长的玻璃纤维增强聚丙烯级产品,用于注塑和挤压。化学耦合到聚丙烯基体上的长玻璃纤维具有优异的机械性能,如高强度、高刚度和良好的冲击性能。由于其优良的性能组合,这种材料可以在许多应用中替代其他工程塑料或金属合金。这种材料的一个重要价值是在潮湿条件或水接触时不会改变其机械性能。该产品提供标准黑色9502。 Fibremod GB215HP is a 20 % long glass fibre reinforced polypropylene grade intended for injection moulding and extrusion. The long glass fibres, chemically coupled to the polypropylene matrix, are providing outstanding mechanical properties such as high strength, high stiffness and excellent impact behaviour. Due to its excellent combination of properties this material can substitute in many applications other engineering plastics or metal alloys. A significant value of this material is the fact that it does not change its mechanical properties at humid conditions or water contact. The product is available in standard black 9502. Applications Fibremod GB215HP has been developed especially for demanding applications in the automotive industry. Dashboard carriers Structural seat parts Door module carriers Special Features Fibremod GB215HP is suitable for processing with special foaming technologies. High heat stabilised |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.04 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
230℃,2.16kg 230℃,2.16kg |
2.0 | g/10min | ISO 1133 |
收缩率 Shrinkage rate 2 |
Internal Method | ||
TD:2.0 mm TD:2.0 mm |
0.55 | % | 内部方法 |
MD:2.0 mm MD:2.0 mm |
0.10 | % | 内部方法 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
|||
注塑成型 injection molding |
5300 | MPa | ISO 527-1-2 |
拉伸强度 tensile strength |
|||
断裂,注塑成型 Fracture, injection molding |
MPa | ISO 527-2 | |
拉伸应变 Tensile strain |
|||
断裂,注塑成型 Fracture, injection molding |
% | ISO 527-2 | |
弯曲模量 Bending modulus 3 |
|||
注塑成型 injection molding 3 |
MPa | ISO 178 | |
弯曲强度 bending strength |
|||
注塑成型 injection molding |
MPa | ISO 178 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
ISO 179/1eA | ||
-20℃,注塑成型 -20 ℃, injection molding |
kJ/m² | ISO 179/1eA | |
23℃,注塑成型 23 ℃, injection molding |
kJ/m² | ISO 179/1eA | |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
ISO 179/1eU | ||
-20℃,注塑成型 -20 ℃, injection molding |
kJ/m² | ISO 179/1eU | |
23℃,注塑成型 23 ℃, injection molding |
kJ/m² | ISO 179/1eU | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ISO 180/1A | ||
-20℃,注塑成型 -20 ℃, injection molding |
kJ/m² | ISO 180-1A | |
23℃,注塑成型 23 ℃, injection molding |
kJ/m² | ISO 180-1A | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
维卡软化温度 Vicat Softening Temp |
℃ | ISO 306/B | |
Melt Energy Melt Energy |
kJ/kg | ISO 11357 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
雾化 atomization |
|||
16 hr,100℃ 16 hr,100℃ |
mg | DIN 75201 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
排放 discharge |
µgC/g | VDA 277 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 150x80x2 mm |
3 0,079 in/min |
【新闻资讯】查看全部
国内首套己内酰胺制己二胺装置开车成功
2022-05-09 5月5日,宁夏瑞泰科技股份有限公司尼龙66新材料项目一次性开车成功,这标志着国内首套己内酰胺制己二胺装置一次性开车成功。 1、 己内酰胺制己二胺工艺 尼龙66的主要原料为己二酸 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |