牌号简介 About |
---|
GELOY™ HRA170D resin是一种具有永久抗静电性能的PC-ASA混合物。它通常用于需要防锈性能和高冲击保持力的应用中。GELOY™ HRA170D resin通常用于各种室外和室内应用,需要卓越的热老化性能和颜色稳定性。 GELOY HRA170D resin is a PC-ASA blend with permanent antistatic behavior. It is typically used in applications that require antidust properties and high impact retention. GELOY HRA170D resin is typically used in various outdoor and indoor applications requiring superior heat aging properties and colour stability. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.16 | g/cm³ | ASTM D792, ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
220℃,10.0kg 220℃,10.0kg |
8.5 | g/10min | ASTM D1238 |
260℃,5.0kg 260℃,5.0kg |
30 | g/10min | ASTM D1238 |
220℃,10.0kg 220℃,10.0kg |
8.0 | g/10min | ISO 1133 |
熔体体积流动速率 Melt Volume Rate |
ISO 1133 | ||
220℃,10 kg 220℃,10 kg |
8.00 | cm³/10min | |
260℃,5 kg 260℃,5 kg |
cm³/10min | ||
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength 12 |
ISO 179/1eA | ||
-30℃ -30℃ |
kJ/m² | ||
23℃ 23℃ |
kJ/m² | ||
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
-30℃ -30℃ |
J/m | ASTM D256 | |
23℃ 23℃ |
J/m | ASTM D256 | |
-30℃ -30℃ 13 |
kJ/m² | ISO 180-1A | |
23℃ 23℃ 14 |
kJ/m² | ISO 180-1A | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火,64 mm跨距 0.45 MPa, unannealed, 64 mm span 15 |
℃ | ISO 75-2/Bf | |
1.8 MPa,未退火,3.2 mm 1.8 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
1.8 MPa,未退火,64 mm跨距 1.8 MPa, unannealed, 64 mm span 16 |
℃ | ISO 75-2/Af | |
维卡软化温度 Vicat Softening Temp |
|||
A50 A50 |
℃ | ISO 306/A50 | |
-- -- |
℃ | ISO 306/A120 | |
B50 B50 |
℃ | ISO 306 | |
B120 B120 |
℃ | ISO 306/B120 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | IEC 60093 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D Shaw's D |
ISO 868 | ||
洛氏硬度 Rockwell hardness |
|||
L 级 Level L |
ISO 2039-2 | ||
球压硬度 Ball hardness |
|||
H358/30 H358/30 |
MPa | ISO 2039-1 | |
拉伸模量 Tensile modulus |
|||
-- -- 1 |
MPa | ASTM D638 | |
-- -- |
MPa | ISO 527-1-2 | |
拉伸强度 tensile strength |
|||
屈服 yield 2 |
MPa | ASTM D638 | |
屈服 yield 3 |
MPa | ASTM D638 | |
屈服 yield |
MPa | ISO 527-2/5 | |
屈服 yield |
MPa | ISO 527-2/50 | |
断裂 fracture 4 |
MPa | ASTM D638 | |
断裂 fracture 5 |
MPa | ASTM D638 | |
断裂 fracture |
MPa | ISO 527-2/5 | |
断裂 fracture |
MPa | ISO 527-2/50 | |
拉伸应变 Tensile strain |
|||
屈服 yield 7 |
% | ASTM D638 | |
屈服 yield |
% | ISO 527-2/5 | |
屈服 yield |
% | ISO 527-2/50 | |
断裂 fracture 8 |
% | ASTM D638 | |
断裂 fracture 9 |
% | ASTM D638 | |
断裂 fracture |
% | ISO 527-2/50 | |
弯曲模量 Bending modulus 10 |
MPa | ISO 178 | |
弯曲强度 bending strength 11 |
MPa | ISO 178 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 0.20 in/min |
3 类型 1, 0.20 in/min |
4 类型 1, 2.0 in/min |
5 0.079 in/min |
6 Yield |
7 80*10*4 sp=62mm |
8 80*10*4 |
9 80*10*4 mm |
【新闻资讯】查看全部
朗盛公司一季度业绩表现微弱EBITDA超预期
2016-05-19 5月17日,特殊化学品公司朗盛宣布上调2016财年的业绩预期,预计本财年常规业务范围内息税折旧及摊销前利润(EBITDA)将达到9亿至9.5亿欧元,较此前8.8亿至9.3亿欧元的预期有所上调。 今年一季度,朗盛常规业务范围内EBITDA达到了2.62亿欧元,相比去年该季度的2.29亿欧元,大幅增长约14%。 朗盛管理董事会主席常牧天表示,上调全年财务预期得益于一季度良好的业绩表现,且第二季度开端也很好。据介绍,朗盛一季度业绩表现良好,主要是因为销量的增长,产 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |