牌号简介 About |
---|
SAMAT 5000(+)是以磷和氮为阻燃剂的无卤阻燃聚丙烯(PP)。炭化和气相阻燃机理起到阻燃性能的作用。可燃性可达到UL94-V0(0.75mm、1.5mm、3.0mm),在70°C下浸水168h(UL746C),GWIT 750°C、GWFI 960°C,具有成品密度低、烟度低、对模具腐蚀小的特点。5000(+)通过UL测试,符合RoHS、SVHC、PFOS和PFOA、16P、无卤和PAH的要求。 5000(+) is halogen-free flame retardant polypropylene with phosphorus and nitrogen as the flame retardant elements. Carbonize and expansion mechanism play the flame retardant performance. The flammability can reach UL94-V0 (0.75mm, 1.5mm and 3.0mm), and passed 70°Cx168 hours water immersion test (UL746C), glow-wire test meets GWIT750°C and GWFI960°C. 5000(+) has the characteristics of low density of finished products, low smoke, less corrosion to the mould etc. 5000(+) halogen free flame retardant PP have UL certification, and meet the requirements of RoHS, SVHC, PFOS & PFOA, 16P, Halogen-free, PAHs...etc. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.06 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
230℃,2.16kg 230℃,2.16kg |
10 | g/10min | ASTM D1238 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
|||
屈服 yield |
16.0 | MPa | ASTM D638 |
拉伸应变 Tensile strain |
|||
断裂 fracture |
300 | % | ASTM D638 |
弯曲模量 Bending modulus |
1560 | MPa | ASTM D790 |
弯曲强度 bending strength |
MPa | ASTM D790 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
J/m | ASTM D256 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ASTM D648 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 , UL 746C | ||
0.75 mm 0.75 mm |
UL 94 , UL 746C | ||
1.50 mm 1.50 mm |
UL 94 , UL 746C | ||
3.00 mm 3.00 mm |
UL 94 , UL 746C |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Flammability after water-boiling testing at 70°C for 168 hours |
【新闻资讯】查看全部 ![]()
工业环氧树脂外面有什么,你晓得吗?
2016-09-07 研究者们发现,具有多用途的工业环氧树脂中包含多种成分,如双酚A环氧氯丙烷、结晶二氧化硅、碳黑、碳酸钙、四乙烯五胺、三-(二甲胺基甲基)苯酚、苯乙醇、二氧化钛和硫酸钡等。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |