PET，LOFEX® A5110对比PET，Skyrol® SH76物性表,价格行情_搜料

牌号信息	LOFEX® A5110 物性表 PET & 韩国乐天指导价格：暂无塑料库存：缺货	Skyrol® SH76 物性表 PET & 韩国SK化学指导价格：暂无塑料库存：缺货
牌号简介	Lofex A5110聚酯薄膜经拉伸强度、适当的延伸率和热收缩率等性能优异的单侧电晕处理后，薄膜呈雾状。因其具有优异的运行性能，易于用合适的产品进行处理，故可采用离型膜。另外，它是一种可以根据客户需求进行厚度控制的产品。 LOFEX ® A5110 Polyester film is hazy and one side corona treated with excellent properties by tensile strength, proper elongation and the thermal contraction rate. It can use by release film because it has excellent run, easy treatment by suitable product. Also, it is a product that thickness control is possible according to customer needs.	Skyrol® SH76是一种光学透明薄膜，具有良好的处理和尺寸稳定性。SH76广泛用作微胶片、投影仪胶片、复合膜等的基片。 Skyrol® SH76 is an optically clear film with good handling and dimensional stability properties. SH76 is widely used as substrates for micro film, overhead projector film, laminating film and the like.

产品描述
厂家：	韩国乐天 LOTTE	韩国SK化学 SKC
类别：	PET PET	PET PET
填料：
用途：	薄膜,工业应用	薄膜,层压板
性能特点：	机械强度好 Good Rigidity	易加工,尺寸稳定性好,光学性能 Excellent Processability,Good Dimensional Stability,Optical performance
加工条件：

技术参数

物理性能
PHYSICAL LOFEX® A5110 Skyrol® SH76 单位
UNIT 测试方法
TEST METHOD

密度
Density g/cm³ ASTM D1505

收缩率(MD：150℃，0.075 mm，30 min)
Shrinkage % 内部方法

收缩率(MD：150℃，0.087 mm，30 min)
Shrinkage % 内部方法

收缩率(TD：150℃，0.075 mm，30 min)
Shrinkage % 内部方法

收缩率(TD：150℃，0.087 mm，30 min)
Shrinkage % 内部方法

表面张力(100.0 µm)
surface tension mN/m

表面张力(50.0 µm)
surface tension mN/m

表面张力(75.0 µm)
surface tension mN/m

薄膜
LOFEX® A5110 Skyrol® SH76 单位
UNIT 测试方法
TEST METHOD

F5(MD：100.0 µm)
F5 MPa ASTM D882

F5(MD：50.0 µm)
F5 MPa ASTM D882

F5(MD：75.0 µm)
F5 MPa ASTM D882

F5(TD：100.0 µm)
F5 MPa ASTM D882

F5(TD：50.0 µm)
F5 MPa ASTM D882

F5(TD：75.0 µm)
F5 MPa ASTM D882

拉伸应变(MD，断裂，100 µm)
Tensile strain % ASTM D882

拉伸应变(MD，断裂，50 µm)
Tensile strain % ASTM D882

拉伸应变(MD，断裂，75 µm)
Tensile strain % ASTM D882

拉伸应变(MD，断裂，87 µm)
Tensile strain % ASTM D882

拉伸应变(TD，断裂，100 µm)
Tensile strain % ASTM D882

拉伸应变(TD，断裂，50 µm)
Tensile strain % ASTM D882

拉伸应变(TD，断裂，75 µm)
Tensile strain % ASTM D882

拉伸应变(TD，断裂，87 µm)
Tensile strain % ASTM D882

拉伸强度(MD，屈服，100 µm)
tensile strength MPa ASTM D882

拉伸强度(MD，屈服，50 µm)
tensile strength MPa ASTM D882

拉伸强度(MD，屈服，75 µm)
tensile strength MPa ASTM D882

拉伸强度(MD，屈服，87 µm)
tensile strength MPa ASTM D882

拉伸强度(TD，屈服，100 µm)
tensile strength MPa ASTM D882

拉伸强度(TD，屈服，50 µm)
tensile strength MPa ASTM D882

拉伸强度(TD，屈服，75 µm)
tensile strength MPa ASTM D882

拉伸强度(TD，屈服，87 µm)
tensile strength MPa ASTM D882

光学性能
OPTICAL LOFEX® A5110 Skyrol® SH76 单位
UNIT 测试方法
TEST METHOD

光泽度(60°，100 µm)
gloss ASTM D523

光泽度(60°，50.0 µm)
gloss ASTM D523

光泽度(60°，75.0 µm)
gloss ASTM D523

光泽度(75.0 µm)
gloss ASTM D523

光泽度(87.0 µm)
gloss ASTM D523

透光率(100 µm)
Light Transmission % ASTM D1003

透光率(50.0 µm)
Light Transmission % ASTM D1003

透光率(75.0 µm)
Light Transmission % ASTM D1003

透光率(87.0 µm)
Light Transmission % ASTM D1003

雾度(100 µm)
Haze % ASTM D1003

雾度(50 µm)
Haze % ASTM D1003

雾度(75.0 µm)
Haze % ASTM D1003

雾度(87 µm)
Haze % ASTM D1003

补充信息
LOFEX® A5110 Skyrol® SH76 单位
UNIT 测试方法
TEST METHOD

Surface Treatment
Surface Treatment

热收缩(MD，30 min：150℃，100.0 µm)
Thermal shrinkage % 内部方法

热收缩(MD，30 min：150℃，50.0 µm)
Thermal shrinkage % 内部方法

热收缩(MD，30 min：150℃，75.0 µm)
Thermal shrinkage % 内部方法

热收缩(TD，30 min：150℃，100.0 µm)
Thermal shrinkage % 内部方法

热收缩(TD，30 min：150℃，50.0 µm)
Thermal shrinkage % 内部方法

热收缩(TD，30 min：150℃，75.0 µm)
Thermal shrinkage % 内部方法

机械性能
MECHANICAL LOFEX® A5110 Skyrol® SH76 单位
UNIT 测试方法
TEST METHOD

摩擦系数(与自身 - 动态)
Frictional coefficient ASTM D1894

摩擦系数(与自身 - 静态)
Frictional coefficient ASTM D1894

备注

1 一般属性：这些不能被视为规格。

2 87 µm

3 75 µm