牌号简介 About |
---|
PET+PBT,44%玻璃纤维/矿物,注塑,LD,高热尺寸稳定性 POCAN® DPT7140LDS 000000 PET+PBT, 44 % glass fibers/mineral, injection molding, LDS, high thermal dimension stability POCAN® DPT7140LDS 000000 PET+PBT, 44 % glass fibers/mineral, injection molding, LDS, high thermal dimension stability POCAN® DPT7140LDS 000000 PET+PBT, 44 % glass fibers/mineral, injection molding, LDS, high thermal dimension stability |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.74 | g/cm³ | ISO 1183 |
表观密度 Apparent density |
1.00 | g/cm³ | ISO 60 |
熔体体积流动速率 Melt Volume Rate |
|||
280℃,2.16 kg 280℃,2.16 kg |
21.0 | cm³/10min | ISO 1133 |
收缩率 Shrinkage rate |
|||
TD:120℃,2.0 mm TD:120℃,2.0 mm 3 |
0.20 | % | |
TD:280℃,2.0 mm TD:280℃,2.0 mm 4 |
0.70 | % | |
MD:120℃,2.0 mm MD:120℃,2.0 mm 3 |
% | ||
MD:280℃,2.0 mm MD:280℃,2.0 mm 4 |
% | ||
粘度值 Viscosity value |
|||
降低的粘度 Reduced viscosity |
ml/g | ISO 1628 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
|||
23℃ 23℃ |
MPa | ISO 527-1-2 | |
拉伸强度 tensile strength |
|||
断裂,23℃ Fracture, 23 ℃ |
MPa | ISO 527-2/5 | |
拉伸应变 Tensile strain |
|||
断裂,23℃ Fracture, 23 ℃ |
% | ISO 527-2/5 | |
弯曲模量 Bending modulus 5 |
|||
23℃ 23℃ 5 |
MPa | ISO 178-A | |
弯曲强度 bending strength 5 |
|||
23℃ 23℃ 5 |
MPa | ISO 178-A | |
弯曲应变 Bending strain 6 |
% | ISO 178/A | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
-30℃ -30℃ |
kJ/m² | ||
23℃ 23℃ |
kJ/m² | ||
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
|||
-30℃ -30℃ |
kJ/m² | ||
23℃ 23℃ |
kJ/m² | ||
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
-30℃ -30℃ |
kJ/m² | ||
23℃ 23℃ |
kJ/m² | ||
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
|||
-30℃ -30℃ |
kJ/m² | ||
23℃ 23℃ |
kJ/m² | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
维卡软化温度 Vicat Softening Temp |
|||
B120 B120 |
℃ | ISO 306/B120 | |
熔融温度 Melting temperature 7 |
℃ | ISO 11357-3 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD:23~55℃ MD:23~55℃ |
1/℃ | ||
TD:23~55℃ TD:23~55℃ |
1/℃ | ||
导热系数 Thermal conductivity coefficient |
|||
23℃ 23℃ |
W/m/K | ISO 8302 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | IEC 60093 | |
体积电阻率 Volume resistivity |
|||
23℃ 23℃ |
ohms·cm | IEC 60093 | |
介电强度 Dielectric strength |
|||
23 ℃,1 mm 23 ℃,1 mm |
kV/mm | IEC 60243-1 | |
相对电容率 Relative permittivity |
|||
23℃,100 Hz 23℃,100 Hz |
|||
23℃,1 MHz 23℃,1 MHz |
|||
耗散因数 Dissipation factor |
|||
23℃,100 Hz 23℃,100 Hz |
|||
23℃,1 MHz 23℃,1 MHz |
|||
相比漏电起痕指数 Compared to the leakage tracing index |
|||
解决方案 A Solution A |
V | IEC 60112 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 | ||
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
ISO Shortname ISO Shortname |
备注 |
---|
3. 60x60x2mm, 4 hr |
4. 60x60x2mm, 110°C MT, 600 bar |
5. 2.0 mm/min |
6. 2 mm/min |
7. 10°C/min |
【新闻资讯】查看全部
7月乘用车降幅收窄5.5个百分点!车市下滑,但车规级LED需求高速增长?
2019-08-20 据乘联会发布的7月数据,2019年7月,中国乘用车市场零售148.5万辆,同比下降5.0%,1-7月累积零售量1143.9万辆,同比下降8.8%。 车市多云,何时转晴? 国五清库存,以及新能源补贴退坡, |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |