牌号简介 About |
---|
HEPLA®H2000 cm树脂是聚苯醚(PPE)和聚酰胺(PA)树脂的混合物,填充矿物,适合注塑成型。导电性水平得到优化,允许无底漆静电喷涂。HEPLA®H2000 cm提高了冲击/延伸率,矿物含量使材料能够用于结构应用,取代金属或热固性树脂。这种材料只有黑色的。 |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.24 | g/cm³ | ASTM D792 |
密度 Density |
1.24 | g/cm³ | ISO 1183 |
Moisture Absorption Moisture Absorption |
|||
平衡,23℃, 50% RH Equilibrium, 23 ℃, 50% RH |
0.7 | % | ISO 62 |
Saturation, 23℃ Saturation, 23℃ |
3.6 | % | ISO 62 |
收缩率 Shrinkage rate |
|||
MD:3.20 mm MD:3.20 mm |
0.7 to 0.9 | % | NFD Method |
熔体质量流动速率 Melt Flow Rate |
|||
280℃,5.0 kg 280℃,5.0 kg |
g/10 min | ASTM D1238 | |
熔体体积流动速率 Melt Volume Rate |
|||
220℃,5.0 kg 220℃,5.0 kg |
cm3/10min | ISO 1133 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
MPa | ISO 527-2/1 | |
Tensile Modulus, 5.0 mm/min Tensile Modulus, 5.0 mm/min |
MPa | ASTM D638 | |
Tensile Stress, yield, Type I Tensile Stress, yield, Type I |
|||
5.0 mm/min 5.0 mm/min |
MPa | ASTM D638 | |
Tensile Stress, break, Type I Tensile Stress, break, Type I |
|||
5.0 mm/min 5.0 mm/min |
MPa | ASTM D638 | |
Tensile Strain, yield, Type I Tensile Strain, yield, Type I |
|||
5.0 mm/min 5.0 mm/min |
% | ASTM D638 | |
Tensile Strain, break, Type I Tensile Strain, break, Type I |
|||
5.0 mm/min 5.0 mm/min |
% | ASTM D638 | |
拉伸强度 tensile strength |
|||
屈服 yield |
MPa | ISO 527-2/5 | |
拉伸强度 tensile strength |
|||
断裂 fracture |
MPa | ISO 527-2/5 | |
拉伸应变 Tensile strain |
|||
屈服 yield |
% | ISO 527-2/5 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ISO 527-2/5 | |
Flexural Modulus, 2.0 mm/min Flexural Modulus, 2.0 mm/min |
MPa | ISO 178 | |
Flexural Modulus, 50.0 mm Span Flexural Modulus, 50.0 mm Span |
|||
1.3 mm/min 1.3 mm/min |
MPa | ASTM D790 | |
Flexural Stress, yield Flexural Stress, yield |
|||
2.0 mm/min 2.0 mm/min |
MPa | ASTM D790 | |
Flexural Stress, break Flexural Stress, break |
|||
50.0 mm Span, 1.3 mm/min 50.0 mm Span, 1.3 mm/min |
MPa | ASTM D790 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度, 23℃ Impact strength of cantilever beam notch, 23 ℃ |
J/m | ASTM D256 | |
Unnotched Izod Impact, -30℃ Unnotched Izod Impact, -30℃ |
J/m | ASTM D4812 | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
80*10*4 , 23℃ 80*10*4 , 23℃ |
kJ/m2 | ISO 180/1A | |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
|||
80*10*4 ,-30℃ 80*10*4 ,-30℃ |
kJ/m2 | ISO 180/1A | |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
80*10*4, 23℃ 80*10*4, 23℃ |
kJ/m2 | ISO 179/1eA | |
飞镖冲击强度 Dart impact strength |
|||
23℃, Total Energy 23℃, Total Energy |
J | ASTM D3763 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
Bf,0.45 MPa Flatw 80*10*4 sp=64mm Bf,0.45 MPa Flatw 80*10*4 sp=64mm |
℃ | ISO 75/Bf | |
0.45MPa,未退火,3.2mm 0.45MPa, unannealed, 3.2mm |
℃ | ||
维卡软化温度 Vicat Softening Temp |
|||
B50 B50 |
℃ | ASTM D1525, ISO 306 | |
B120 B120 |
℃ | ISO 306 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
Flow : -40 to 40℃ Flow : -40 to 40℃ |
1/℃ | ASTM E831, ISO 11359-2 | |
Transverse : -40 to 40℃ Transverse : -40 to 40℃ |
1/℃ | ASTM E831, ISO 11359-2 |
备注 | |||
---|---|---|---|
暂无数据 |
【新闻资讯】查看全部
两项石墨烯领域国家标准发布
2022-02-25 近日,石墨烯领域的两项国家标准 GB/T41067-2021 《纳米技术石墨烯粉体中硫、氟、氯、溴含量的测定 燃烧离子色谱法》和GB/T41068-2021《纳米技术石墨烯粉体中水溶性阴离子含量的测定离子 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |