牌号简介 About |
---|
L-670M是由Spheripol工艺生产的聚丙烯无规共聚物。该等级设计用于潜在的最终用途,包括BOPP薄膜上的挤压涂层。硬度好,加工性好,颜料分散性好,结合强度好 L-670M is a polypropylene random copolymer manufactured by under the Spheripol process. This grade is designed to potential end use applications include Extrusion coating on BOPP film. Good stiffness, Good processability, Good pigment dispersion, Good bond strength |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.900 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
230℃,2.16kg 230℃,2.16kg |
28 | g/10min | ASTM D1238 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃ 23℃ |
57 | J/m | ASTM D256 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
65.0 | ℃ | ASTM D648 |
维卡软化温度 Vicat Softening Temp |
126 | ℃ | ISO 306 |
熔融温度 Melting temperature |
℃ | 内部方法 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
洛氏硬度 Rockwell hardness |
|||
R 级 R-level |
ASTM D785 | ||
拉伸强度 tensile strength |
|||
屈服 yield |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ASTM D638 | |
弯曲模量 Bending modulus |
MPa | ASTM D790 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
500亿级产业园入列晋重点工程 新日恒力携手大股东加码生物基新材料
2021-10-18 搜料网资讯: 近日,山西省重点工程领导组办公室公布了2021年省级重点工程中期调整项目名单,此前备受业界关注的上海中能集团京沪同生物基新材料产业园(下称中能新材料产业园) |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |