牌号简介 About |
---|
Viton® A-700是一种“A族”胶聚合物,已证明易于加工。这种口香糖提供:良好的压缩成型流动性,良好的模具释放性,减少模具污染,提高压缩定型阻力,改善撕裂性能,应用于燃油系统的首选材料,如喷油器O形环,O形环的压缩成型,垫圈和其他密封装置,挤压电线,型材和管道,或压延当使用树胶聚合物混合物时,用溶液将织物涂层和其他基材与其他聚合物混合以改变粘度。 Viton® A-700 is an "A-family" gum polymer that has demonstrated easy processing. This gum provides: Good flow for compression molding Good mold release Less mold fouling Improved compression set resistance, and Improved tear properties Applications Preferred material for fuel systems, such as fuel injector O-rings Compression molding of O-rings, gaskets, and other sealing devices Extruded cords, profiles and tubing, or calendered sheets, when a blend of gum polymers are used Solution coatings of fabrics and other substrates Blending with other polymers for viscosity modifications |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.77 | g/cm³ | ASTM D792 |
门尼粘度 Mooney viscosity |
|||
ML 1+10,121℃ ML 1+10,121℃ |
74 | MU | ASTM D1646 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
ASTM D2240 | ||
邵氏 A,23℃ Shore A, 23 ℃ 2 |
62 | ASTM D2240 | |
邵氏 A,23℃ Shore A, 23 ℃ 3 |
74 | ASTM D2240 | |
邵氏 A,23℃ Shore A, 23 ℃ 4 |
73 | ASTM D2240 | |
邵氏 A,23℃ Shore A, 23 ℃ 5 |
ASTM D2240 | ||
邵氏 A,23℃ Shore A, 23 ℃ 6 |
ASTM D2240 | ||
邵氏 A,23℃ Shore A, 23 ℃ 7 |
ASTM D2240 | ||
邵氏 A,23℃ Shore A, 23 ℃ 8 |
ASTM D2240 | ||
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
ASTM D412 | ||
100% 应变,23℃ 100% strain, 23 ℃ 9 |
MPa | ASTM D412 | |
100% 应变,23℃ 100% strain, 23 ℃ 10 |
MPa | ASTM D412 | |
100% 应变,23℃ 100% strain, 23 ℃ 11 |
MPa | ASTM D412 | |
100% 应变,23℃ 100% strain, 23 ℃ 12 |
MPa | ASTM D412 | |
100% 应变,23℃ 100% strain, 23 ℃ 13 |
MPa | ASTM D412 | |
100% 应变,23℃ 100% strain, 23 ℃ 14 |
MPa | ASTM D412 | |
100% 应变,23℃ 100% strain, 23 ℃ 15 |
MPa | ASTM D412 | |
拉伸强度 tensile strength |
ASTM D412 | ||
屈服,23℃ Yield, 23 ℃ 9 |
MPa | ASTM D412 | |
屈服,23℃ Yield, 23 ℃ 10 |
MPa | ASTM D412 | |
屈服,23℃ Yield, 23 ℃ 11 |
MPa | ASTM D412 | |
屈服,23℃ Yield, 23 ℃ 12 |
MPa | ASTM D412 | |
屈服,23℃ Yield, 23 ℃ 13 |
MPa | ASTM D412 | |
屈服,23℃ Yield, 23 ℃ 14 |
MPa | ASTM D412 | |
屈服,23℃ Yield, 23 ℃ 15 |
MPa | ASTM D412 | |
拉伸应变 Tensile strain |
ASTM D412 | ||
断裂,23℃ Fracture, 23 ℃ 9 |
% | ASTM D412 | |
断裂,23℃ Fracture, 23 ℃ 10 |
% | ASTM D412 | |
断裂,23℃ Fracture, 23 ℃ 11 |
% | ASTM D412 | |
断裂,23℃ Fracture, 23 ℃ 12 |
% | ASTM D412 | |
断裂,23℃ Fracture, 23 ℃ 13 |
% | ASTM D412 | |
断裂,23℃ Fracture, 23 ℃ 14 |
% | ASTM D412 | |
断裂,23℃ Fracture, 23 ℃ 15 |
% | ASTM D412 | |
撕裂强度 tear strength 16 |
|||
23℃ 23℃ 16 |
kN/m | ASTM D624 | |
压缩形变 Compression deformation |
ASTM D395B | ||
150℃,70 hr 150℃,70 hr |
% | ASTM D395B | |
200℃,70 hr 200℃,70 hr |
% | ASTM D395B | |
200℃,168 hr 200℃,168 hr |
% | ASTM D395B | |
232℃,22 hr 232℃,22 hr |
% | ASTM D395B | |
老化性能 Aging performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积变化 Volume change |
ASTM D471 | ||
23℃,168 hr,in M15(Fuel C/Methanol 85/15) 23℃,168 hr,in M15(Fuel C/Methanol 85/15) |
% | ASTM D471 | |
200℃,70 hr,in IRM 902 Oil 200℃,70 hr,in IRM 902 Oil |
% | ASTM D471 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 20 in/min, 老化 M15 (Fuel C/Methanol 85/15) 168 hr 在 73°F |
3 20 in/min, 老化 70 hr 在 392°F |
4 20 in/min, 老化 IRM 902 Oil 70 hr 在 392°F |
5 20 in/min, 老化 168 hr 在 392°F |
6 20 in/min, 老化 24 hr 在 450°F |
7 20 in/min, 老化 70 hr 在 482°F |
8 20 in/min, 老化 168 hr 在 482°F |
9 C 模具 |
10 老化 M15 (Fuel C/Methanol 85/15) 168 hr 在 73°F |
11 老化 70 hr 在 392°F |
12 老化 IRM 902 Oil 70 hr 在 392°F |
13 老化 168 hr 在 392°F |
14 老化 24 hr 在 450°F |
15 老化 70 hr 在 482°F |
16 老化 168 hr 在 482°F |
【新闻资讯】查看全部
新秀丽收购轻奢品牌塔米 创塑料制造之共赢
2016-04-08 行李箱制造公司新秀丽(Samsonite)近日收购了美国轻奢品牌塔米控股公司。新秀丽称,这宗交易的部分动因来自硬壳塑料行李箱领域的创新潜力。 新秀丽收购高端行李箱制造企业塔米的交易总价达18亿美元,新秀丽首席执行官拉美西-塔恩瓦拉(Ramesh Tainwala)称,并购完成后,新秀丽将向高端商务旅行箱细分市场拓展,也将使美国塔米公司更加国际化。 新秀丽收购轻奢品牌塔米 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |