牌号简介 About |
---|
MDPEHT514是以己烯为共聚单体,采用浆环工艺生产的中密度聚乙烯。MDPE HT 514是一种具有优良机械性能的半高分子量聚乙烯。分子量分布广泛,加工性能优异。MDPE HT 514可单独使用、混合或共挤在各种吹塑薄膜应用中:消费者、工业、食品或卫生包装。 MDPE HT 514 is a medium density polyethylene produced by slurry loop process with hexene as co-monomer. MDPE HT 514 is a semi-high molecular weight polyethylene giving excellent mechanical properties. It shows a broad molecular weight distribution ensuring outstanding processability. MDPE HT 514 can be used alone, blended or coextruded in a wide variety of blown film applications : consumer, industrial, food or hygiene packaging. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.938 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
ISO 1133 | ||
190℃,2.16kg 190℃,2.16kg |
0.15 | g/10min | ISO 1133 |
190℃,21.6kg 190℃,21.6kg |
14 | g/10min | ISO 1133 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
弯曲模量 Bending modulus |
740 | MPa | ISO 178 |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
20 40 | µm | |
拉伸强度 tensile strength |
ISO 527-3 | ||
MD,屈服,20 µm,吹塑薄膜 MD, yield, 20 µ m, blow molded film |
MPa | ISO 527-3 | |
TD,屈服,20 µm,吹塑薄膜 TD, yield, 20 µ m, blow molded film |
MPa | ISO 527-3 | |
MD,屈服,40 µm,吹塑薄膜 MD, yield, 40 µ m, blow molded film |
MPa | ISO 527-3 | |
TD,屈服,40 µm,吹塑薄膜 TD, yield, 40 µ m, blow molded film |
MPa | ISO 527-3 | |
拉伸强度 tensile strength |
ISO 527-3 | ||
MD,断裂,20 µm,吹塑薄膜 MD, fracture, 20 µ m, blow molded film |
MPa | ISO 527-3 | |
TD,断裂,20 µm,吹塑薄膜 TD, fracture, 20 µ m, blow molded film |
MPa | ISO 527-3 | |
MD,断裂,40 µm,吹塑薄膜 MD, fracture, 40 µ m, blow molded film |
MPa | ISO 527-3 | |
TD,断裂,40 µm,吹塑薄膜 TD, fracture, 40 µ m, blow molded film |
MPa | ISO 527-3 | |
拉伸应变 Tensile strain |
ISO 527-3 | ||
MD,断裂,20 µm,吹塑薄膜 MD, fracture, 20 µ m, blow molded film |
% | ISO 527-3 | |
TD,断裂,20 µm,吹塑薄膜 TD, fracture, 20 µ m, blow molded film |
% | ISO 527-3 | |
MD,断裂,40 µm,吹塑薄膜 MD, fracture, 40 µ m, blow molded film |
% | ISO 527-3 | |
TD,断裂,40 µm,吹塑薄膜 TD, fracture, 40 µ m, blow molded film |
% | ISO 527-3 | |
落锤冲击 Drop hammer impact |
ISO 7765-1 | ||
20 µm,吹塑薄膜 20 µ m, blow molded film |
g | ISO 7765-1 | |
40 µm,吹塑薄膜 40 µ m, blow molded film |
g | ISO 7765-1 | |
埃尔曼多夫抗撕强度 Elmandorf tear strength |
ISO 6383-2 | ||
MD:20 µm,吹塑薄膜 MD: 20 µ m, blow molded film |
N | ISO 6383-2 | |
TD:20 µm,吹塑薄膜 TD: 20 µ m, blow molded film |
N | ISO 6383-2 | |
MD:40 µm,吹塑薄膜 MD: 40 µ m, blow molded film |
N | ISO 6383-2 | |
TD:40 µm,吹塑薄膜 TD: 40 µ m, blow molded film |
N | ISO 6383-2 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
维卡软化温度 Vicat Softening Temp |
℃ | ISO 306 | |
熔融温度 Melting temperature |
℃ | ISO 11357-3 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
GS加德士投运丽水裂解装置
2021-07-05 搜料网资讯: 近日,韩国GS加德士公司宣布,该公司已如期投运了位于丽水的一套新建混合进料蒸汽裂解装置。新建裂解装置乙烯产能70万吨/年、丙烯30万吨/年,使用液化石油气(LPG)、石 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |