24FS040是一种采用高压管法生产的薄膜级低密度聚乙烯(LDPE)。它可以相当容易地在任何传统的LDPE挤出机上挤出。该聚合物在制造过程中与必要的添加剂混合,以获得良好的表面滑动和容易在两层薄膜之间打开。 24FS040 is a film grade Low Density Polyethylene (LDPE) produced by high pressure tubular process. It can be extruded with considerable ease on any conventional LDPE extruder. The polymer has been blended with necessary additives during manufacture to obtain good surface slip and easy openability between two layers of the film. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.922 | g/cm³ | ASTM D1505 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
4.0 | g/10min | ASTM D1238 |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
ASTM D882 | ||
MD,断裂,40 µm,吹塑薄膜 MD, fracture, 40 µ m, blow molded film |
18.0 | MPa | ASTM D882 |
TD,断裂,40 µm,吹塑薄膜 TD, fracture, 40 µ m, blow molded film |
16.0 | MPa | ASTM D882 |
拉伸应变 Tensile strain |
ASTM D882 | ||
MD,断裂,40 µm,吹塑薄膜 MD, fracture, 40 µ m, blow molded film |
250 | % | ASTM D882 |
TD,断裂,40 µm,吹塑薄膜 TD, fracture, 40 µ m, blow molded film |
% | ASTM D882 | |
落锤冲击 Drop hammer impact |
|||
40 µm,吹塑薄膜 40 µ m, blow molded film |
g | ASTM D1709-A |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
美开发最适宜火箭喷嘴的“绿色”碳纤维
2016-12-01 最近,美国阿拉巴马大学汉茨维尔分校(UAH)的研究人员开发了一种绿色环保的碳纤维制造新方法,用来生产耐烧蚀的火箭喷嘴和隔热罩,该技术已经获得了美国专利。 UAH旋翼机系统工程与仿真中心的副教授、与NASA签约35年了的研究员William Kaukler博士介绍,该工艺绿色环保,所有边角料皆可回收。 Kaukler博士是从美国陆军航空和导弹研究发展工程中心(AMRDEC)获得资助,并在UAH的可靠性与失效分析实验室开展相关研究工作的。 新型碳 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |