牌号简介 About |
---|
AMPLIFY™ TY 1354功能性聚合物是马来酸酐接枝(MAH)聚合物。在软包装的连接层中,AMPLIFY™ TY 1354功能性聚合物促进聚乙烯与阻隔性聚合物(如聚酰胺和其他极性基质)的粘合。主要特点:对聚酰胺有良好的粘附力,优异的物理性能,吹塑和铸膜的工艺和使用温度范围广泛,符合:美国FDA 21 CFR 175.105(c)(5)欧盟,2011年10月,详细信息请参考法规。 AMPLIFY™ TY 1354 Functional Polymer is a maleic anhydride grafted (MAH) polymer. In tie layers for flexible packaging, AMPLIFY TY 1354 Functional Polymer promotes adhesion of Polyethylene to barrier polymers such as polyamide and other polar substrates. Main Characteristics: Excellent adhesion to polyamide Excellent physical properties Wide range of process and service temperature For blown and cast film Complies with: US FDA 21 CFR 175.105 (c)(5) EU, No 10/2011 Consult the regulations for complete details. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.920 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
3.0 | g/10min | ASTM D1238,ISO 1133 |
MAH 接枝水平 MAH grafting level 2 |
Low | 内部方法 | |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
膜耐刺穿性 Membrane puncture resistance |
|||
51 µm 51 µm |
9.51 | J/cm³ | 内部方法 |
割线模量 Secant modulus |
ASTM D882 | ||
2% 正割,MD:51 µm 2% secant, MD: 51 µ m |
214 | MPa | ASTM D882 |
2% 正割,TD:51 µm 2% secant, TD: 51 µ m |
MPa | ASTM D882 | |
拉伸强度 tensile strength |
ASTM D882 | ||
MD,屈服,51 µm MD, yield, 51 µ m |
MPa | ASTM D882 | |
TD,屈服,51 µm TD, yield, 51 µ m |
MPa | ASTM D882 | |
MD,断裂,51 µm MD, fracture, 51 µ m |
MPa | ASTM D882 | |
TD,断裂,51 µm TD, fracture, 51 µ m |
MPa | ASTM D882 | |
拉伸应变 Tensile strain |
ASTM D882 | ||
MD,断裂,51 µm MD, fracture, 51 µ m |
% | ASTM D882 | |
TD,断裂,51 µm TD, fracture, 51 µ m |
% | ASTM D882 | |
落锤冲击 Drop hammer impact |
|||
51 µm 51 µm |
g | ASTM D1709 | |
埃尔曼多夫抗撕强度 Elmandorf tear strength 3 |
ASTM D1922 | ||
MD:51 µm MD:51 µm |
g | ASTM D1922 | |
TD:51 µm TD:51 µm |
g | ASTM D1922 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 | |
熔融温度 Melting temperature |
|||
DSC DSC |
℃ | 内部方法 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
|||
45°,50.8 µm 45°,50.8 µm |
ASTM D2457 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Low: <0.25 wt%, Medium 0.25-0.5, High >0.5 wt% |
3 Method B |
【新闻资讯】查看全部
塑料光纤将助力光纤到户
2015-11-25 塑料光纤的使用,在“光纤到户”的后期阶段解决了“最后100米”的接入难题,实现了光纤到桌面,满足了人们对全光通信的要求。并且其相对铜线缆低碳、节能、环保,符合国家宽带接入网和光进铜退的发展战略。 塑料光纤的芯层材料是由聚碳酸酯、聚甲基丙烯酸甲酯、高透明聚合物如聚苯乙烯组成,外皮则由氟塑料和PMMA等一些光导纤维组成。其大芯径50/125um和62。5/125um的石英玻璃多模光纤相比,塑料光纤的芯径高达200~1000um,其接续时可使用不带光纤定位套筒的便宜注塑塑料连接器 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |