DSM的Somos® NanoTool在传统的立体光刻机上生产出坚固、坚硬、耐高温的复合材料部件。这种材料填充了大量的非晶纳米颗粒,可以更快地进行加工。与其他复合立体光刻材料相比,该材料具有优异的侧壁质量和良好的细节分辨率。应用Somos® NanoTool的光滑表面质量和高初始模量使其成为一种优良的金属电镀树脂-一个不断增长的应用,节省了时间和金钱作为替代金属原型。它还非常适合制造具有优异的高耐热性的坚固、坚硬的零件,包括用于航空航天和汽车应用的风洞模型,以及用于注塑的快速模具。 DSM's Somos® NanoTool produces strong, stiff, high-temperature resistant composite parts on conventional stereolithography machines. This material is heavily filled with non-crystalline nanoparticles allowing for faster processing. It exhibits superior sidewall quality, along with excellent detail resolution compared to other composite stereolithography materials. Applications Somos® NanoTool's smooth surface quality and high initial modulus make it an excellent resin for metal plating-a growing application which saves time and money as an alternative to metal prototypes. It's also ideal for creating strong, stiff parts with excellent high heat resistance, including wind tunnel models for aerospace and automotive applications, as well as rapid tooling for injection molding. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.65 | g/cm³ | |
吸水率 Water absorption rate |
ASTM D570 | ||
平衡 balance 2 |
0.23 | % | ASTM D570 |
平衡 balance 3 |
0.15 到 0.16 | % | ASTM D570 |
粘度 viscosity |
|||
30℃ 30℃ |
2.50 | Pa·s | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ASTM D256A | ||
-- -- 2 |
12 到 15 | J/m | ASTM D256-A |
-- -- 3 |
J/m | ASTM D256-A | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
ASTM D648 | ||
0.45 MPa,未退火 0.45 MPa, unannealed 2 |
℃ | ASTM D648 | |
0.45 MPa,未退火 0.45 MPa, unannealed 3 |
℃ | ASTM D648 | |
1.8 MPa,未退火 1.8 MPa, unannealed 3 |
℃ | ASTM D648 | |
1.8 MPa,未退火 1.8 MPa, unannealed 2 |
℃ | ASTM D648 | |
玻璃化转变温度 Glass transition temperature |
ASTM E1545 | ||
-- -- 2 |
℃ | ASTM E1545 | |
-- -- 3 |
℃ | ASTM E1545 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD MD |
|||
-40 到 0℃ -40 to 0 ℃ 3 |
cm/cm/℃ | ASTM E831 | |
0 到 50℃ 0 to 50 ℃ 3 |
cm/cm/℃ | ASTM E831 | |
0 到 50℃ 0 to 50 ℃ 2 |
cm/cm/℃ | ASTM E831 | |
50 到 100℃ 50 to 100 ℃ 3 |
cm/cm/℃ | ASTM E831 | |
50 到 100℃ 50 to 100 ℃ 2 |
cm/cm/℃ | ASTM E831 | |
100 到 150℃ 100 to 150 ℃ 2 |
cm/cm/℃ | ASTM E831 | |
100 到 150℃ 100 to 150 ℃ 3 |
cm/cm/℃ | ASTM E831 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
介电强度 Dielectric strength 2 |
kV/mm | ASTM D149 | |
介电常数 Dielectric constant |
|||
60 Hz 60 Hz 2 |
ASTM D150 | ||
60 Hz 60 Hz 3 |
ASTM D150 | ||
1 kHz 1 kHz 2 |
ASTM D150 | ||
1 kHz 1 kHz 3 |
ASTM D150 | ||
1 MHz 1 MHz 2 |
ASTM D150 | ||
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
Critical Exposure Critical Exposure |
mJ/cm² | ||
渗透深度 Penetration depth |
µm | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness 2 |
|||
邵氏 D Shaw's D 2 |
ASTM D2240 | ||
拉伸模量 Tensile modulus |
ASTM D638 | ||
-- -- 2 |
MPa | ASTM D638 | |
-- -- 3 |
MPa | ASTM D638 | |
拉伸强度 tensile strength |
ASTM D638 | ||
-- -- 2 |
MPa | ASTM D638 | |
-- -- 3 |
MPa | ASTM D638 | |
拉伸应变 Tensile strain 2 |
|||
断裂 fracture 2 |
% | ASTM D638 | |
弯曲模量 Bending modulus |
ASTM D790 | ||
-- -- 2 |
MPa | ASTM D790 | |
-- -- 3 |
MPa | ASTM D790 | |
弯曲强度 bending strength |
ASTM D790 | ||
-- -- 2 |
MPa | ASTM D790 | |
-- -- 3 |
MPa | ASTM D790 | |
泊松比 Poisson's ratio |
ASTM D638 | ||
-- -- 2 |
ASTM D638 | ||
-- -- 3 |
ASTM D638 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 UV Postcure & Thermal Postcure |
3 UV Postcure |
【新闻资讯】查看全部
工程塑料:静等节后市场风云变幻!
2021-04-26 搜料网资讯: 上游原料的短缺造成了目前工程料市场一货难求的局面,有些生产厂家甚至一而再再而三的连发数张涨价函。这不,在即将到来的五一假期,小编又收到了来自巴斯夫、朗 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |