| 牌号简介 About |
|---|
| Vydyne® 49H是通用的冲击改性PA66树脂。天然的,它是热稳定的,以提高抵抗高温。Vydyne® 49H的热稳定包装是为了在预期持续或延长高温暴露的应用中使用时提供热耐久性而制定的。Vydyne® 49H是公认的所有加工和性能优势固有的PA66与提高冲击强度。该树脂具有高熔点、良好的表面润滑性、耐磨性和对许多化学品、机器和汽车油、溶剂和汽油的抵抗力等工程性能的良好平衡组合。 Vydyne 49H is general-purpose, impact-modified PA66 resin. Available in natural, it is heat-stabilized for improved resistance to elevated temperatures. The heat stabilization package for Vydyne 49H was formulated to provide thermal endurance when used in applications in which continuous or extended high-temperature exposure is anticipated. Vydyne 49H is recognized for all the processing and property advantages inherent to PA66 with the addition of improved impact strength. This resin offers a well balanced combination of engineering properties characterized by high melt point, good surface lubricity, abrasion resistance and resistance to many chemicals, machine and motor oils, solvents and gasoline. |
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
1.11 | g/cm³ | ISO 1183 |
|
收缩率 Shrinkage |
ISO 294-4 | ||
|
TD:2.0 mm TD:2.0 mm |
1.6 | % | ISO 294-4 |
|
MD:2.0 mm MD:2.0 mm |
1.8 | % | ISO 294-4 |
|
吸水率 Water Absorption |
|||
|
平衡,50% RH Balance, 50% RH |
注册或登录后
所有资料免费
|
% | ISO 62 |
|
23℃,24hr 23℃,24hr |
注册或登录后
所有资料免费
|
% | ISO 62 |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸模量 Tensile modulus |
注册或登录后
所有资料免费
|
MPa | ISO 527-2 |
|
拉伸强度 tensile strength |
注册或登录后
所有资料免费
|
||
|
断裂 fracture |
注册或登录后
所有资料免费
|
MPa | ISO 527-2 |
|
屈服 yield |
注册或登录后
所有资料免费
|
MPa | ISO 527-2 |
|
拉伸应变 Tensile strain |
注册或登录后
所有资料免费
|
||
|
断裂 fracture |
注册或登录后
所有资料免费
|
% | ISO 527-2 |
|
弯曲模量 Flexural Modulus |
注册或登录后
所有资料免费
|
MPa | ISO 178 |
|
弯曲强度 Flexural Strength |
注册或登录后
所有资料免费
|
MPa | ISO 178 |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
简支梁缺口冲击强度 Charpy Notched Impact Strength |
注册或登录后
所有资料免费
|
ISO 179 | |
|
-40℃ -40℃ |
注册或登录后
所有资料免费
|
kJ/m² | ISO 179 |
|
-30℃ -30℃ |
注册或登录后
所有资料免费
|
kJ/m² | ISO 179 |
|
23℃ 23℃ |
注册或登录后
所有资料免费
|
kJ/m² | ISO 179 |
|
简支梁无缺口冲击强度 Charpy Unnotched Impact strength |
注册或登录后
所有资料免费
|
ISO 179 | |
|
-30℃ -30℃ |
注册或登录后
所有资料免费
|
ISO 179 | |
|
23℃ 23℃ |
注册或登录后
所有资料免费
|
ISO 179 | |
|
悬臂梁缺口冲击强度 Izod Notched Impact strength |
注册或登录后
所有资料免费
|
ISO 180 | |
|
-40℃ -40℃ |
注册或登录后
所有资料免费
|
kJ/m² | ISO 180 |
|
-30℃ -30℃ |
注册或登录后
所有资料免费
|
kJ/m² | ISO 180 |
|
23℃ 23℃ |
注册或登录后
所有资料免费
|
kJ/m² | ISO 180 |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 HDT |
注册或登录后
所有资料免费
|
||
|
1.8 MPa,未退火 1.8 MPa, unannealed |
注册或登录后
所有资料免费
|
℃ | ISO 75-2/A |
|
0.45 MPa,未退火 0.45 MPa, unannealed |
注册或登录后
所有资料免费
|
℃ | ISO 75-2/B |
|
熔融温度 Melting temperature |
注册或登录后
所有资料免费
|
℃ | ISO 11357-3 |
|
线性热膨胀系数 Coeff.of linear therm expansion |
注册或登录后
所有资料免费
|
||
|
TD:23~55℃,2 mm TD:23~55℃,2 mm |
注册或登录后
所有资料免费
|
1/℃ | ISO 11359-2 |
|
MD:23~55℃,2 mm MD:23~55℃,2 mm |
注册或登录后
所有资料免费
|
1/℃ | ISO 11359-2 |
|
相对温度指数 Relative temperature index |
注册或登录后
所有资料免费
|
||
|
电气性能 ELECTRICAL |
注册或登录后
所有资料免费
|
UL 746 | |
|
0.75 mm 0.75 mm |
注册或登录后
所有资料免费
|
℃ | UL 746 |
|
1.5 mm 1.5 mm |
注册或登录后
所有资料免费
|
℃ | UL 746 |
|
3.0 mm 3.0 mm |
注册或登录后
所有资料免费
|
℃ | UL 746 |
|
强度机械性能 Strength mechanical performance |
注册或登录后
所有资料免费
|
UL 746 | |
|
0.75 mm 0.75 mm |
注册或登录后
所有资料免费
|
℃ | UL 746 |
|
1.5 mm 1.5 mm |
注册或登录后
所有资料免费
|
℃ | UL 746 |
|
3.0 mm 3.0 mm |
注册或登录后
所有资料免费
|
℃ | UL 746 |
|
冲击机械性能 Impact mechanical performance |
注册或登录后
所有资料免费
|
UL 746 | |
|
0.75 mm 0.75 mm |
注册或登录后
所有资料免费
|
℃ | UL 746 |
|
1.5 mm 1.5 mm |
注册或登录后
所有资料免费
|
℃ | UL 746 |
|
3.0 mm 3.0 mm |
注册或登录后
所有资料免费
|
℃ | UL 746 |
|
电气性能 ELECTRICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
体积电阻率 Volume resistivity |
注册或登录后
所有资料免费
|
||
|
0.75 mm 0.75 mm |
注册或登录后
所有资料免费
|
ohms·cm | IEC 60093 |
|
介电强度 Dielectric strength |
注册或登录后
所有资料免费
|
||
|
1 mm 1 mm |
注册或登录后
所有资料免费
|
kV/mm | ASTM D149 |
|
耐电弧性 Arc resistance |
注册或登录后
所有资料免费
|
||
|
3.0 mm 3.0 mm |
注册或登录后
所有资料免费
|
ASTM D495 | |
|
相比漏电起痕指数 Comparative Tracking Index |
注册或登录后
所有资料免费
|
||
|
3.00 mm 3.00 mm |
注册或登录后
所有资料免费
|
V | IEC 60112 |
|
高电弧燃烧指数(HAI) High Arc Burning Index (HAI) |
注册或登录后
所有资料免费
|
UL 746 | |
|
0.75 mm 0.75 mm |
注册或登录后
所有资料免费
|
UL 746 | |
|
1.5 mm 1.5 mm |
注册或登录后
所有资料免费
|
UL 746 | |
|
3.0 mm 3.0 mm |
注册或登录后
所有资料免费
|
UL 746 | |
|
高电压电弧起痕速率 High Voltage Arc Track Rate |
注册或登录后
所有资料免费
|
||
|
HVTR HVTR |
注册或登录后
所有资料免费
|
UL 746 | |
|
热丝引燃 Hot wire ignition |
注册或登录后
所有资料免费
|
||
|
HWI HWI |
注册或登录后
所有资料免费
|
UL 746 | |
|
0.75 mm 0.75 mm |
注册或登录后
所有资料免费
|
UL 746 | |
|
1.5 mm 1.5 mm |
注册或登录后
所有资料免费
|
UL 746 | |
|
3.0 mm 3.0 mm |
注册或登录后
所有资料免费
|
UL 746 | |
|
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
阻燃等级 Flame Class Rating |
注册或登录后
所有资料免费
|
UL 94 | |
|
0.75 mm 0.75 mm |
注册或登录后
所有资料免费
|
UL 94 | |
|
1.50 mm 1.50 mm |
注册或登录后
所有资料免费
|
UL 94 | |
|
3.00 mm 3.00 mm |
注册或登录后
所有资料免费
|
UL 94 | |
|
灼热丝可燃性指数 Glow Wire Flammability Index(GWFI) |
注册或登录后
所有资料免费
|
IEC 60695-2-12 | |
|
0.75 mm 0.75 mm |
注册或登录后
所有资料免费
|
℃ | IEC 60695-2-12 |
|
1.5 mm 1.5 mm |
注册或登录后
所有资料免费
|
℃ | IEC 60695-2-12 |
|
3.0 mm 3.0 mm |
注册或登录后
所有资料免费
|
℃ | IEC 60695-2-12 |
|
灼热丝起燃温度 Glow Wire Ignitability Temperature(GWIT) |
注册或登录后
所有资料免费
|
IEC 60695-2-13 | |
|
0.75 mm 0.75 mm |
注册或登录后
所有资料免费
|
℃ | IEC 60695-2-13 |
|
1.5 mm 1.5 mm |
注册或登录后
所有资料免费
|
℃ | IEC 60695-2-13 |
|
3 mm 3 mm |
注册或登录后
所有资料免费
|
℃ | IEC 60695-2-13 |
|
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
汽车材料 Automotive materials |
注册或登录后
所有资料免费
|
||
|
thickness d = 1 mm thickness d = 1 mm |
注册或登录后
所有资料免费
|
FMVSS 302 | |
| 备注 |
|---|
| 1 一般属性:这些不能被视为规格。 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |















支付宝
微信支付