牌号简介 About |
---|
PPE + PS共混物。未填充的适用于型材挤压。吸水率低。水解稳定性。尺寸稳定性。典型应用包括反渗透系统的管道。 PPE+PS blend. Unfilled. Suitable for profile extrusion. Low water absorption. Hydrolytic stability. Dimensional stability. Typical applications include tubes for reverse osmosis systems. |
产品描述 Product Description
厂家:沙特沙伯基础 SABIC
类别:PPO(PPE)+PS PPO(PPE)+PS
用途:型材;管件;
加工条件:挤出 Extrusion
性能特点: 防火阻燃等级HB; 尺寸稳定性好; 吸水率低; 耐水解; Good Dimensional Stability,Hydrolysis stability,Low or no water absorption,HB
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.06 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
280℃,5.0kg 280℃,5.0kg |
8.5 | g/10min | ASTM D1238 |
熔体体积流动速率 Melt Volume Rate |
|||
280℃,5 kg 280℃,5 kg |
8.70 | cm³/10min | ISO 1133 |
收缩率 Shrinkage rate |
|||
MD:3.2 mm MD:3.2 mm |
0.50 to 0.70 | % | 内部方法 |
吸水率 Water absorption rate |
|||
24hr 24hr |
0.060 | % | ASTM D570 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
ISO 179/2C | ||
-30℃ -30℃ |
kJ/m² | ISO 179/2C | |
23℃ 23℃ |
kJ/m² | ISO 179/2C | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ASTM D256 | ||
-30℃ -30℃ |
J/m | ASTM D256 | |
23℃ 23℃ |
J/m | ASTM D256 | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch 6 |
ISO 180/1A | ||
-30℃ -30℃ |
kJ/m² | ISO 180-1A | |
23℃ 23℃ |
kJ/m² | ISO 180-1A | |
装有测量仪表的落镖冲击 Dart impact equipped with measuring instruments |
|||
23℃,Total Energy 23℃,Total Energy |
J | ASTM D3763 | |
落锤冲击 Drop hammer impact |
ASTM D3029 | ||
-40℃ -40℃ |
J | ASTM D3029 | |
-30℃ -30℃ |
J | ASTM D3029 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
ASTM D648 | ||
1.8 MPa,未退火,3.2 mm 1.8 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
1.8 MPa,未退火,6.4 mm 1.8 MPa, unannealed, 6.4 mm |
℃ | ASTM D648 | |
0.45 MPa,未退火,3.2 mm 0.45 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
0.45 MPa,未退火,6.4 mm 0.45 MPa, unannealed, 6.4 mm |
℃ | ASTM D648 | |
维卡软化温度 Vicat Softening Temp |
|||
B50 B50 |
℃ | ISO 306 | |
B120 B120 |
℃ | ISO 306/B120 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD:-40~95℃ MD:-40~95℃ |
1/℃ | ASTM E831 | |
相对温度指数 Relative temperature index |
|||
电气性能 Electrical performance |
℃ | UL 746 | |
强度机械性能 Strength mechanical performance |
℃ | UL 746 | |
冲击机械性能 Impact mechanical performance |
℃ | UL 746 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
介电强度 Dielectric strength |
|||
3.2 mm,在油中 3.2 mm in oil |
kV/mm | ASTM D149 | |
介电常数 Dielectric constant |
ASTM D150 | ||
50 Hz 50 Hz |
ASTM D150 | ||
60 Hz 60 Hz |
ASTM D150 | ||
耗散因数 Dissipation factor |
ASTM D150 | ||
50 Hz 50 Hz |
ASTM D150 | ||
60 Hz 60 Hz |
ASTM D150 | ||
耐电弧性 Arc resistance 7 |
ASTM D495 | ||
相比漏电起痕指数 Compared to the leakage tracing index |
UL 746 | ||
高电弧燃烧指数(HAI) High Arc Burning Index (HAI) |
UL 746 | ||
高电压电弧起痕速率 High voltage arc marking rate |
|||
HVTR HVTR |
UL 746 | ||
热丝引燃 Hot wire ignition |
|||
HWI HWI |
UL 746 | ||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
|||
1.50 mm 1.50 mm |
UL 94 | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus 2 |
MPa | ASTM D638 | |
拉伸模量 Tensile modulus |
MPa | ISO 527-1-2 | |
拉伸强度 tensile strength |
|||
断裂 fracture |
MPa | ASTM D638 | |
断裂 fracture |
MPa | ISO 527-2 | |
屈服 yield 3 |
MPa | ASTM D638 | |
屈服 yield |
MPa | ISO 527-2 | |
拉伸应变 Tensile strain |
|||
断裂 fracture 4 |
% | ASTM D638 | |
断裂 fracture |
% | ISO 527-2 | |
屈服 yield |
% | ASTM D638 | |
屈服 yield |
% | ISO 527-2 | |
弯曲模量 Bending modulus |
ASTM D790 | ||
50 mm跨距 50 mm span 4 |
MPa | ASTM D790 | |
100 mm跨距 100 mm span 5 |
MPa | ASTM D790 | |
弯曲模量 Bending modulus |
MPa | ISO 178 | |
弯曲强度 bending strength |
MPa | ISO 178 | |
弯曲强度 bending strength |
ASTM D790 | ||
屈服,50 mm跨度 Yield, 50 mm span 4 |
MPa | ASTM D790 | |
屈服,100 mm跨度 Yield, 100 mm span 5 |
MPa | ASTM D790 | |
洛氏硬度 Rockwell hardness |
|||
R 级 R-level |
ASTM D785 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 0,20 in/min |
3 类型 1, 2,0 in/min |
4 0,051 in/min |
5 0,10 in/min |
6 80*10*4 |
7 钨电极 |
【新闻资讯】查看全部
帝斯曼收买尚善新资料 中国光伏市场布大局
2017-02-23 荷兰皇家帝斯曼集团(DSM)近日在沪召开新闻发布会,宣布全资收购苏州尚善新材料科技有限公司。 尚善科技是一家采用共挤技术生产高性能、创新性太阳能光伏 (PV) 背板的生产商。双方未披露此项收购的财务细节。 “此次收购不仅与帝斯曼的可持续发展战略相一致,也契合中国能源发展十三五规划。它进一步证明了帝斯曼集团对于中国清洁和绿色能源市场的支持。”帝斯曼中国总裁蒋惟明博士说。 得益于可再生能源方面的政策支持,2016年中国光伏发电新增装机容量和累计装 |
帝斯曼收买尚善新资料 中国光伏市场布大局 荷兰皇家帝斯曼集团公司(DSM)近日在沪举办记者招待会,公布国有独资收购苏州市尚善新型材料高新科技有限责任公司。 尚善高新科技是一家选用共挤技术性生产制造性能卓越、创新能力光伏发电 (PV) 侧板的制造商。彼此未公布该项收购的会计关键点。 “本次收购不但与帝斯曼的可持续发展观发展战略相一致,也切合中国电力能源发展趋势十三五规划。它进一步证实了帝斯曼集团公司针对中国清理和清洁能源市场的适用。”帝斯曼中国首席总裁蒋惟明博士研究生说。 归功于可再生资源层面的政策支持,2016年中国太阳能发电增加年发电量和总计年发电量各自做到3454亿千瓦和7742亿千瓦,二项指标值均居全世界第一位。依据《能源发展“十三五”规划》的规定,2020年中国太阳能发电站经营规模将做到1.一亿KW。 国际金融公司(International Finance Corporation-IFC)最近公布的《新兴市场的储能发展趋势和机遇》汇报也称,未来五年储能在新兴市场将以40%的年增长率快速发展趋势。印尼和中国将各自推动东亚和亚洲地区的储能市场发展趋势。 业内预估,在中国政府部门全力促进经济发展可持续发展观的情况下,中国光伏行业和太阳能电池市场市场前景仍然开朗。针对看中这一市场的跨国公司来讲,根据收购当地技术性领跑公司从供应链管理上下游进入市场,有利于其能够更好地掌握中国太阳能发电市场的机会。 来源于:CPRJ 中国塑胶硫化橡胶 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
价格走势图
开始时间:
结束时间:
材料厂家:
【牌号齐全,内容全面】
全网共2500+项牌号+上游原料单体+原油价格,最长可追溯近20年价格行情
【精准,及时,权威!】
专业团队挖掘行情信息,第一时间发布行情
抱歉!该牌号暂无认证数据。
免责声明:参考价格是搜料网根据网络大数据拟合分析的结果,仅供参考。实际成交价取决但不限于以下因素:下单时间,付款方式,交货方式,数量,税费,色号,产地,项目信息。
- NORYL树脂光伏接线盒
- 2022-10-18 0
- NORYL树脂具有优秀的尺寸稳定性、电气和热性能,能耐受-40°C至140°C的温度,长期在户外的湿热环境使用后,还可保持85%以上的性能,且具有低翘曲特性,满足对接线盒材料的高要求
- 阅读全文
NORYL树脂光伏接线盒
1-NORYL树脂具有优秀的尺寸稳定性、电气和热性能,能耐受-40°C至140°C的温度;
2-长期在户外的湿热环境使用后,可保持85%以上的性能;
3-具有低翘曲特性,满足对接线盒材料的高要求,如设计的灵活性、无氯无溴阻燃、易安装性等;
4-可降低系统成本,符合严格的全球监管标准。
2-长期在户外的湿热环境使用后,可保持85%以上的性能;
3-具有低翘曲特性,满足对接线盒材料的高要求,如设计的灵活性、无氯无溴阻燃、易安装性等;
4-可降低系统成本,符合严格的全球监管标准。
收起
抱歉!暂无数据。