牌号简介 About |
---|
Shin Etsu KE-1950-30是一种液体注射成型硅胶。它作为两种成分提供,以1:1的比例混合,以确保轻松和准确的混合。KE-1950-30的粘度很低,可以很容易地泵送到大多数注塑系统中。高温快速固化时间。室温下使用寿命长。典型应用O型环。- Diaphragms。盖帽。橡胶辊。连接器填料。其他电气部件 Shin-Etsu KE-1950-30 is a liquid injection molding silicone. It is supplied as two components which are mixed in a 1:1 ratio to ensure easy and accurate blending. The viscosity of KE-1950-30 is low enough to allow easy pumping through most injection molding systems. Rapid cure time at elevated temperature. Long pot life at room temperature. Typical Applications O-rings. - Diaphragms. Capping. Rubber rollers. Connector packings. Other electrical parts |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.10 | g/cm³ | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
32 | ||
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
8.80 | MPa | |
100% 应变 100% strain |
0.696 | MPa | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
700 | % | |
撕裂强度 tear strength 2 |
kN/m | ||
压缩形变 Compression deformation |
|||
180℃,22 hr 180℃,22 hr |
% | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
后固化时间 Post curing time |
|||
200℃ 200℃ |
hr | ||
Uncured Properties Uncured Properties |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
固化时间 Curing time |
hr |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 B 模具 |
【新闻资讯】查看全部
洋垃圾制止入境倒计时 塑料产业机遇与应战并存
2017-12-13 随着《禁止洋垃圾入境推进固体废物进口管理制度改革实施方案》的逐步落实,洋垃圾禁止入境进入最后阶段。对于塑料行业而言,机遇与挑战并存,业内人士认为,废塑料的今后发展可能呈现四大趋势。 洋垃圾禁止入境倒计时 塑料产业机遇与挑战并存 距离 2017年07月27日发布的《禁止洋垃圾入境推进固体废物进口管理制度改革实施方案》过去了3个月。 随着方案的逐步落实,洋垃圾进口也进入最后阶段 改革开放的几十年来 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |