牌号简介 About |
---|
LDF-0218A是一种经过认证的优质产品,专门为需要优良机械性能的工业应用(如重型包装袋、运输袋、收缩包装托盘罩、建筑、农业和温室)挤压重型吹塑薄膜而设计。LDF-0218A具有优异的加工性能,薄膜具有高韧性、高冲击和撕裂强度,以及优良的收缩性能。LDF-0218A不含防堵剂、紫外线稳定剂和防滑剂。LDF-0218A符合FDA法规21CFR 177.1520(c)2.1+2.2和大多数有关使用聚乙烯与食品接触的国际法规。 LDF-0218A is a certified prime grade specially designed for EXTRUSION of heavy duty Blown Film for industrial applications requiring excellent mechanical properties, such as heavy duty sacks, shipping bags, shrink wrapping pallet hoods, construction, agriculture and greenhouses. LDF-0218A features excellent processability and films exhibit high toughness, high impact and tear strength, and excellent shrink properties. LDF-0218A contains no antiblock, no UV stabilizer and no slip. LDF-0218A complies with FDA regulation 21CFR 177.1520 (c ) 2.1 + 2.2 and most international regulations concerning the use of Polyethylene in contact with food articles. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.918 | g/cm³ | ASTM D1505 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
0.25 | g/10min | ASTM D1238 |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
51 | µm | |
割线模量 Secant modulus |
|||
1% 正割,TD,51 µm 1% secant, TD, 51 µ m |
207 | MPa | ASTM D882 |
1% 正割,MD,51 µm 1% secant, MD, 51 µ m |
172 | MPa | ASTM D882 |
拉伸强度 tensile strength |
|||
TD,断裂,51 µm TD, fracture, 51 µ m |
MPa | ASTM D882 | |
TD,屈服,51 µm TD, yield, 51 µ m |
MPa | ASTM D882 | |
MD,断裂,50 µm MD, fracture, 50 µ m |
MPa | ASTM D882 | |
MD,屈服,51 µm MD, yield, 51 µ m |
MPa | ASTM D882 | |
拉伸应变 Tensile strain |
|||
TD,断裂,51 µm TD, fracture, 51 µ m |
% | ASTM D882 | |
MD,断裂,50 µm MD, fracture, 50 µ m |
% | ASTM D882 | |
落锤冲击 Drop hammer impact |
|||
50 µm 50 µm |
g | ASTM D1709-A | |
埃尔曼多夫抗撕强度 Elmandorf tear strength |
|||
MD,50 µm MD,50 µm |
g | ASTM D1922 | |
撕裂强度 tear strength |
|||
TD,51 µm TD,51 µm |
g | ASTM D1922 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
黎明院高性能聚氨酯弹性体技术获奖
2021-07-12 搜料网资讯: 日前,由黎明化工研究设计院有限责任公司自主研发的一种高性能聚氨酯弹性体及其制备方法获第22届中国专利奖银奖。 该专利的技术方案,打破了国外长期垄断局面,解 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |