牌号简介 About |
---|
SABIC® PP QR673K是一种高透明无规共聚物,具有良好的抗静电性能。这一等级结合了改进的美学成品和低温加工能力。部件美观性不受较低温度的影响,从而提供更宽的操作窗口。SABIC® PP QR673K具有优良的脱模特性,具有良好的刚度与冲击比。用途:SABIC® PP QR673K主要用于注塑工艺。SABIC® PP QR673K的目标是透明的应用范围从注射成型的家庭用品,办公室和家庭存储盒,盖子和瓶盖。本文所述产品尤其未经测试,因此未经验证可用于医药/医疗应用。 SABIC® PP QR673K is a highly transparent random copolymer with good antistatic properties. This grade combines improved aesthetics of the finished articles with low temperature processability. Part aesthetics are not affected by the lower temperatures, providing for a broader operating window. The SABIC® PP QR673K results in excellent demoulding characteristics and has a good stiffness to impact ratio. Application: SABIC® PP QR673K is mainly used in injection moulding processes. The SABIC® PP QR673K aims at transparent applications ranging from injection moulded housewares, office & home storage boxes, lids to caps & closures. The product mentioned herein is in particular not tested and therefore not validated for use in pharmaceutical/medical applications. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.905 | g/cm³ | ASTM D792, ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
230℃,2.16kg 230℃,2.16kg |
25 | g/10min | ASTM D1238,ISO 1133 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
0℃ 0℃ |
2.0 | kJ/m² | ISO 179/1fA |
23℃ 23℃ |
6.0 | kJ/m² | ISO 179/1eA |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
0℃ 0℃ |
30 | J/m | ASTM D256-A |
23℃ 23℃ |
J/m | ASTM D256-A | |
0℃ 0℃ |
kJ/m² | ISO 180-1A | |
23℃ 23℃ |
kJ/m² | ISO 180-1A | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ASTM D648 | |
0.45 MPa,未退火 0.45 MPa, unannealed 4 |
℃ | ISO 75-2/Bf | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
1.8 MPa,未退火 1.8 MPa, unannealed 5 |
℃ | ISO 75-2/Af | |
维卡软化温度 Vicat Softening Temp |
|||
-- -- |
℃ | ASTM D1525,ISO 306/A120 6 6 | |
B120 B120 |
℃ | ASTM D1525, ISO 306/B120 7 7 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
雾度 Haze |
% | ASTM D1003 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D Shaw's D |
ISO 868 | ||
洛氏硬度 Rockwell hardness |
|||
R 级 R-level |
ASTM D785 | ||
拉伸模量 Tensile modulus |
|||
1% 正割 1% secant 1 |
MPa | ASTM D638 | |
-- -- |
MPa | ISO 527-2/1A/1 | |
拉伸强度 tensile strength |
|||
屈服 yield 2 |
MPa | ASTM D638 | |
屈服 yield |
MPa | ISO 527-2/1A/50 | |
拉伸应变 Tensile strain |
|||
屈服 yield 3 |
% | ASTM D638 | |
屈服 yield |
% | ISO 527-2/1A/50 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 0.039 in/min |
3 2.0 in/min |
4 testbar 80*10*4mm |
5 标准 B (120°C/h), 压 力1 (10N) |
6 标准 B (120°C/h), 载荷2 (50N) |
【新闻资讯】查看全部
中国化工为何执意收购先正达?
2016-03-02 巴斯夫在参与竞购先正达的多年以前,就已经开始确定了农化战略,在中国进行了上亿欧元的投资和布局,竞争购先正达失败以后,其投资农化的战略依然未变,都是因为中国快速增长的经济,带来的耕地不断减少,和不断增长的人口之间的矛盾,所引发的粮食安全问题越来越严重,而且几十年内根本无法彻底解决。目前,中国只能通过农药、化肥、改良种子与农技等手段,来保证国家粮食安全,尽量减少对粮食进口的依赖。中国的农化市场是巨大的,持续的,增长的。而且多年以后,印度的农化市场也将爆发,要么赶上要么超过中国。中国与印度拥有世 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |