牌号简介 About |
---|
钢管用聚乙烯化合物面漆黑色高密度聚乙烯化合物Lushan EJ-1钢管用聚乙烯化合物面漆用于石油天然气输送管道和高压水管道的2PE/3PE埋地防腐钢管涂层系统或涂层钢塑复合管的防腐材料。系统。它含有分散的炭黑,具有优异的耐候性。钢管面漆用高密度聚乙烯化合物Lushan EJ-1具有加工范围广、与胶粘剂相容性高、力学性能优良等优良性能,钢管面漆用高密度聚乙烯化合物Lushan EJ-1的设计满足下列国家和国际标准的要求,条件是普赖特工业处理方法采用连续质量控制体系,与共聚物胶粘剂树脂芦山L-5R、聚乙烯复合面漆EJ-1、相容粉末环氧树脂配套使用。NFA 49710 CAN/CSA-Z245.21 DIN 30670S草案ISO 21809-1 Polyethylene Compounds for Steel Pipe Top Coats Black high density polyethylene compounds Lushan EJ-1 for steel pipe top coats is used as anti-corrosion material for 2PE/3PE buried against-corrosion steel pipe coating system or coated steel plastic composite pipes in the application of oil &gas transportation pipeline and high pressure water pipeline systems. It contains dispersed carbon black with the purpose of excellent weathering properties. HDPE compounds Lushan EJ-1 for steel pipe top coats has good properties such as widely processing range, high Compatibility with adhesive and excellent mechanical properties, etc. HDPE compounds Lushan EJ-1 for steel pipe top coats is designed to meet with requirements of the following National and International standards, under the condition that appropriate industrial processing method are applied under a continuous quality control system and when used in combination with copolymer adhesive resin Lushan L-5R& polyethylene compound top coats EJ-1 and a compatible powder epoxy. NFA 49710 CAN/CSA-Z245.21 DIN 30670S Draft ISO 21809-1 |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
> 0.940 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
ISO 1133 | ||
190℃,2.16kg 190℃,2.16kg |
> 0.17 | g/10min | ISO 1133 |
190℃,5.0kg 190℃,5.0kg |
1.5 到 2.5 | g/10min | ISO 1133 |
炭黑含量 Carbon black content |
> 2.0 | % | ASTM D1603 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength 2 |
|||
断裂 fracture 2 |
> 20.0 | MPa | ASTM D638 |
拉伸应变 Tensile strain 2 |
|||
断裂 fracture 2 |
% | ASTM D638 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
脆化温度 Embrittlement temperature |
℃ | ASTM D746 | |
维卡软化温度 Vicat Softening Temp |
|||
A50 A50 |
℃ | ISO 306/A50 | |
熔融温度 Melting temperature |
℃ | ISO 11357-3 |
备注 |
---|
2 50 mm/min |
【新闻资讯】查看全部
东营港口岸初次进口大型聚酯塑料主反响器
2017-11-30 近日,一艘载有2台生产聚酯塑料主反应器的韩国籍货轮“HAEBOK”号顺利靠泊东营港。该批设备经东营检验检疫局查验合格后顺利入境,这是东营港口岸首次进口大型化工设备。 该反应器可以令高粘度聚合物的酯交换反应充分进行,得到高品质的聚碳酸酯产品,属于推进化工产业新旧动能转换的国家扶持项目,后期还将有8台该类设备陆续入境。东营地区是全国最大的石油化工产品聚集区,不断推进产业向精细化、高附加值产品转型升级是当前面临的重要任务,是转变经济增长方式、促进 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |