牌号简介 About |
---|
OREVAC IM300是一种顺丁烯二酸酐改性的线性低密度聚乙烯,以颗粒形式提供。应用OREVAC IM300被设计成用作一种高抗冲改性剂,适用于各种工程聚合物,如聚酰胺(PA6、PA66、PA12等)。由于其性质(柔软性、反应性),OREVAC IM300特别适用于需要具有良好加工性的化合物,尤其是在注射中。 OREVAC® IM300 is a maleic anhydride modified linear low-density polyethylene available in pellet form. Applications OREVAC® IM300 has been designed to be used as a high impact modifier for a large range of engineering polymers such as polyamides (PA6, PA66, PA12 etc.). Due to its properties (softness, reactivity), OREVAC ® IM300 is especially suitable when a compound with excellent processability, especially in injection, is required. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.870 | g/cm³ | ISO 1183 , ASTM D1505 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
1.2 | g/10min | ASTM D1238,ISO 1133 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
维卡软化温度 Vicat Softening Temp |
32.0 | ℃ | ISO 306/A , ASTM D1525 2 |
熔融温度 Melting temperature |
112 | ℃ | ISO 11357-3 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
ISO 868 | ||
邵氏 A,1 秒,模压成型 Shore A, 1 second, molded |
78 | ISO 868 | |
邵氏 A,15 秒,模压成型 Shore A, 15 seconds, molded |
ISO 868 | ||
邵氏 D,1 秒,模压成型 Shore D, 1 second, molded |
ISO 868 | ||
邵氏 D,15 秒,模压成型 Shore D, 15 seconds, molded |
ISO 868 | ||
拉伸强度 tensile strength |
|||
断裂,模压成型 Fracture, molded |
MPa | ASTM D638 , ISO 527-2 | |
拉伸应变 Tensile strain |
|||
断裂,模压成型 Fracture, molded |
% | ASTM D638 , ISO 527-2 | |
弯曲模量 Bending modulus |
|||
模压成型 Compression Molding |
MPa | ASTM D790 , ISO 178 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 压 力1 (10N) |
【新闻资讯】查看全部
2019广州军民两用技术配备效果展览会
2019-01-16 2019广州军民两用技术装备成果展览会,时间:2019年5月9日—11日地点:广州·中国进出口商品交易会展馆 [广交会展馆] 为凸显“民参军”战略支撑能力与广东区位优势,开展军地两用技 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |