牌号简介 About |
---|
Bayflex MP-5000是一种固体弹性体,室温下的弯曲模量为5000 psi(35 MPa)。*在反应注射成型(RIM)设备上加工,用于辊、垫圈和密封窗口。该系统结合了快速拆卸时间、良好的拆卸完整性、改进的释放特性和出色的物理性能。与任何产品一样,在给定应用中使用Bayflex MP-5000系统必须由用户提前进行测试(包括现场测试等),以确定其适用性。Bayflex MP-5000是作为两种液体成分提供的配方RIM系统。A组分为二苯基甲烷二异氰酸酯(MDI)预聚物,B组分为聚醚多元醇。注意:在将内容物从桶转移到日计量箱之前,应彻底搅动部件B。 Bayflex MP-5,000 is a solid elastomer which has a flexural modulus of 5,000 psi (35 MPa) at room temperature.* It is processed on reaction injection molding (RIM) equipment and is used for rollers, gaskets, and encapsulated windows. This system combines rapid demold times, excellent integrity at demold, improved release characteristics and outstanding physical properties. As with any product, use of the Bayflex MP-5,000 system in a given application must be tested (including field testing, etc.) in advance by the user to determine suitability. Bayflex MP-5,000 is a formulated RIM system supplied as two liquid components. Component A is a diphenylmethane diisocyanate (MDI) prepolymer, and Component B is a polyether polyol. Note: Component B should be agitated thoroughly prior to transfer of contents from the drum to the day tank. |
产品描述 Product Description
厂家:德国科思创 Covestro
类别:PUR-脂肪族+MDI PUR-脂肪族+MDI
用途:门窗;滚轴;垫圈;
加工条件:反应注射成型 (RIM)
性能特点: 含脱模剂; Good stripping performance
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
|||
-- -- |
0.998 | g/cm³ | ASTM D792 |
-- -- |
1.00 | g/cm³ | ASTM D1622 |
收缩率 Shrinkage rate |
|||
MD:3.0 mm MD:3.0 mm |
1.3 | % | 内部方法 |
吸水率 Water absorption rate |
|||
10days,3.00 mm 10days,3.00 mm |
5.0 | % | 内部方法 |
24hr,3.00 mm 24hr,3.00 mm |
3.3 | % | 内部方法 |
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
ASTM D412 | ||
断裂,3 mm Fracture, 3 mm |
MPa | ASTM D412 | |
断裂,3 mm Fracture, 3 mm |
MPa | ASTM D638 | |
20% 应变 20% strain 2 |
MPa | ASTM D412 | |
50% 应变,3 mm 50% strain, 3 mm 3 |
MPa | ASTM D412 | |
100% 应变,3 mm 100% strain, 3 mm 3 |
MPa | ASTM D412 | |
拉伸应变 Tensile strain |
|||
断裂,3 mm Fracture, 3 mm |
% | ASTM D412 | |
撕裂强度 tear strength 4 |
|||
3.00 mm 3.00 mm 4 |
kN/m | ASTM D624 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
Water Immersion(Length Increase,3.00 mm) Water Immersion(Length Increase,3.00 mm) |
% | 内部方法 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
ASTM D2240 | ||
邵氏 A,3.00 mm Shore A, 3.00 mm |
ASTM D2240 | ||
邵氏 D,3.00 mm Shore D, 3.00 mm |
ASTM D2240 | ||
弯曲模量 Bending modulus |
ASTM D790 | ||
-30℃,3 mm -30℃,3 mm |
MPa | ASTM D790 | |
23℃,3 mm 23℃,3 mm |
MPa | ASTM D790 | |
65℃,3 mm 65℃,3 mm |
MPa | ASTM D790 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD:3 mm MD:3 mm |
1/℃ | ASTM D696 | |
低温脆性 Low temperature brittleness |
|||
-50℃,3.00 mm -50℃,3.00 mm |
ASTM D746 | ||
热固组件 Thermosetting components 5 |
|||
部件 A Component A |
|||
部件 B Component B |
|||
贮藏期限 Storage period |
|||
30℃ 30℃ |
wk | ||
脱模时间 stripping time |
min |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Die C, 20 in/min |
3 C 模具, 20 in/min |
4 C 模具 |
5 105 Index |
【新闻资讯】查看全部
山西推进采空区煤层气开发
2021-08-28 搜料网资讯: 日前从山西省自然资源厅传来消息,自去年底该厅挂牌出让3个煤炭采空区(废弃矿井)煤层气抽采试验区块以来,全省已累计施工抽采井100余口,抽采利用煤层气资源1.28亿立 |
山西推进采空区煤层气开发 搜料网资讯:日前从山西省自然资源厅传来消息,自去年底该厅挂牌出让3个煤炭采空区(废弃矿井)煤层气抽采试验区块以来,全省已累计施工抽采井100余口,抽采利用煤层气资源1.28亿立方米,相当于减排二氧化碳192万吨。 山西是全国重要的能源基地,在提供大量煤炭能源的同时,也产生了许多煤炭采空区(废弃矿井)。据初步调查,全省有开发利用价值的煤炭采空区(废弃矿井)面积约2052平方千米,预测残余煤层气资源量约726亿立方米。近年来,山西出台了一系列政策措施,引导各类市场主体积极参与、有序实施煤炭采空区(废弃矿井)煤层气抽采试验。这也是山西能源革命综合改革试点的一项重要任务。 山西省自然资源厅厅长姚青林表示,下一步将立足不同矿区煤炭采空区(废弃矿井)煤层气资源的配置情况,分类施策,稳步推进抽采试验,并进一步完善相关配套政策,加强对抽采试验的综合保障和依法监管,确保试验取得实效。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
价格走势图
开始时间:
结束时间:
材料厂家:
【牌号齐全,内容全面】
全网共2500+项牌号+上游原料单体+原油价格,最长可追溯近20年价格行情
【精准,及时,权威!】
专业团队挖掘行情信息,第一时间发布行情
抱歉!该牌号暂无认证数据。
免责声明:参考价格是搜料网根据网络大数据拟合分析的结果,仅供参考。实际成交价取决但不限于以下因素:下单时间,付款方式,交货方式,数量,税费,色号,产地,项目信息。
抱歉!暂无数据。
抱歉!暂无数据。