牌号简介 About |
---|
这种线性低密度聚乙烯是一种乙烯-己烯共聚物,为薄膜应用量身定制,需要:卓越的加工特性,特殊的拉伸使用单独或共挤;与其他聚烯烃混合,在薄规格下具有良好的硬度,大量的滑动剂,典型的吹塑薄膜应用包括:共挤混合用于改善拉伸性能的组件薄型应用通用包装典型的铸膜应用包括:外包装共挤 This linear low density polyethylene is an ethylene-hexene copolymer tailored for film applications that require: Excellent processing characteristics Exceptional drawdown Use alone or in coextrusions; blends with other polyolefins Good stiffness at thin gauges High amounts of slip agent Typical blown film applications include: Coextrusions Blend component to improve drawdown Thin gauge applications General purpose packaging Typical cast film applications include: Overwrap Coextrusions |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.919 | g/cm³ | ASTM D1505 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
2.0 | g/10min | ASTM D1238 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
摩擦系数 friction coefficient |
|||
吹塑薄膜 Blown film |
0.70 | ASTM D1894 | |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
割线模量 Secant modulus |
|||
1% 正割,MD:25 µm,吹塑薄膜 1% secant, MD: 25 µ m, blow molded film |
228 | MPa | |
1% 正割,MD:32 µm,铸造薄膜 1% secant, MD: 32 µ m, cast thin film |
200 | MPa | |
1% 正割,TD:25 µm,吹塑薄膜 1% secant, TD: 25 µ m, blow molded film |
MPa | ||
1% 正割,TD:32 µm,铸造薄膜 1% secant, TD: 32 µ m, cast thin film |
MPa | ||
拉伸强度 tensile strength |
|||
MD,断裂,25 µm,吹塑薄膜 MD, fracture, 25 µ m, blow molded film |
MPa | ||
MD,断裂,32 µm,吹塑薄膜 MD, fracture, 32 µ m, blow molded film |
MPa | ||
TD,断裂,25 µm,吹塑薄膜 TD, fracture, 25 µ m, blow molded film |
MPa | ||
TD,断裂,32 µm,吹塑薄膜 TD, fracture, 32 µ m, blow molded film |
MPa | ||
拉伸应变 Tensile strain |
|||
MD,断裂,25 µm,吹塑薄膜 MD, fracture, 25 µ m, blow molded film |
% | ||
MD,断裂,32 µm,挤塑薄膜 MD, fracture, 32 µ m, extruded film |
% | ||
TD,断裂,25 µm,吹塑薄膜 TD, fracture, 25 µ m, blow molded film |
% | ||
TD,断裂,32 µm,挤塑薄膜 TD, fracture, 32 µ m, extruded film |
% | ||
落锤冲击 Drop hammer impact |
|||
25 µm,吹塑薄膜 25 µ m, blow molded film |
g | ||
32 µm,铸造薄膜 32 µ m, cast thin film |
g | ||
埃尔曼多夫抗撕强度 Elmandorf tear strength |
|||
MD:25 µm,吹塑薄膜 MD: 25 µ m, blow molded film |
g | ||
MD:32 µm,铸造薄膜 MD: 32 µ m, cast thin film |
g | ||
TD:25 µm,吹塑薄膜 TD: 25 µ m, blow molded film |
g | ||
TD:32 µm,铸造薄膜 TD: 32 µ m, cast thin film |
g | ||
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
|||
60°,25.4 µm,吹塑薄膜 60 °, 25.4 µ m, blow molded film |
|||
60°,31.8 µm,铸造薄膜 60 °, 31.8 µ m, cast thin film |
|||
雾度 Haze |
|||
25.4 µm,吹塑薄膜 25.4 µ m, blow molded film |
% | ||
31.8 µm,铸造薄膜 31.8 µ m, cast thin film |
% |
备注 | |||
---|---|---|---|
暂无数据 |
【新闻资讯】查看全部
海南精细化工二期工程丙烯腈项目最新进展
2021-05-26 搜料网资讯: 近日,记者走进东方临港产业园看到,多个项目正在加快建设。在海南精细化工二期工程丙烯腈项目(以下简称丙烯腈项目)现场,工人们正顶着烈日,加紧施工,努力确 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |