牌号简介 About |
---|
在复杂金属有机催化剂存在下乙烯气相聚合得到的产物。稳定配方:抗酸剂、抗氧化剂、热稳定剂、加工助剂、分散剂。用途:电缆管道和污水管道的基本元件。技术要求:TU 2211-145-05766801-2008 Product obtained by gas phase polymerization of ethylene with hexane-1 in presence of complex metalorganic catalysts. Stabilization recipe: antacids, antioxydant, heat stabilizer, processing additive, dispersant. Application: base component of a compound for the production of wire conduit and drain pipes. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.946 到 0.950 | g/cm³ | ASTM D1505 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
3.5 到 4.5 | g/10min | ASTM D1238 |
抗环境应力开裂 ESCR(Environmental Stress Cracking Resistance) |
> 1000 | hr | ASTM D1693 |
熔体流比 Melt flow ratio |
|||
MFR 21.6 kg/MFR 5.0 kg MFR 21.6 kg/MFR 5.0 kg |
< 18.0 | ASTM D1238 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
弯曲模量 Bending modulus |
1000 | MPa | ASTM D790 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃ 23℃ |
J/m | ASTM D256 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
帝人与Applied EV公司合作开发用于未来交通的聚碳酸酯太阳能车顶
2021-03-07 搜料网资讯: 帝人与其合作开发伙伴Applied Electric Vehicles开发了一种用于未来汽车的聚碳酸酯太阳能车顶。新型太阳能车顶的表面采用了帝人的Panlite聚碳酸酯树脂玻璃。 帝人利用其在聚 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |