牌号简介 About |
---|
UN315采用Unipol工艺技术制造。UN315具有良好的机械性能、透明度和加工性。 UN315 is manufactured by Unipol process technology. UN315 has good mechanical properties, good Transparency and good processability. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.920 | g/cm³ | ASTM D1505 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
1.1 | g/10min | ASTM D1238 |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
40 | µm | |
拉伸强度 tensile strength |
ASTM D882 | ||
MD,断裂,40 µm,吹塑薄膜 MD, fracture, 40 µ m, blow molded film |
42.2 | MPa | ASTM D882 |
TD,断裂,40 µm,吹塑薄膜 TD, fracture, 40 µ m, blow molded film |
38.2 | MPa | ASTM D882 |
拉伸应变 Tensile strain |
ASTM D882 | ||
MD,断裂,40 µm,吹塑薄膜 MD, fracture, 40 µ m, blow molded film |
% | ASTM D882 | |
TD,断裂,40 µm,吹塑薄膜 TD, fracture, 40 µ m, blow molded film |
% | ASTM D882 | |
落锤冲击 Drop hammer impact |
|||
40 µm,吹塑薄膜 40 µ m, blow molded film |
g | ASTM D1709 | |
撕裂强度 tear strength 2 |
ASTM D1922 | ||
MD,40 µm MD,40 µm |
kN/m | ASTM D1922 | |
TD,40 µm TD,40 µm |
kN/m | ASTM D1922 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
|||
45°,40.0 µm,吹塑薄膜 45 °, 40.0 µ m, blow molded film |
ASTM D2457 | ||
雾度 Haze |
|||
40 µm,吹塑薄膜 40 µ m, blow molded film |
% | ASTM D1003 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Blown Film |
【新闻资讯】查看全部
陶氏三研讨员跻身塑料工程师协会会员
2016-04-20 陶氏化学公司今日宣布该公司三位研究员巴拉特・乔德哈里(Bharat Chaudhary)博士,史蒂芬・高德思(Stéphane Costeux)博士,莫力杜拉・布里・卡普尔(Mridula Babli Kapur)博士入选塑料工程师协会会员。塑料业内最大的ANTEC会议,于2016年 5月23日至25日期间在印第安纳波利斯举行,会议公布了包括三位陶氏员工在内的共12名会员。 陶氏高级副总裁和首席技术官A.N.Sreeram表示:同一年之内公司有三位获此殊荣实属惊喜,布里,巴 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |