牌号简介 About |
---|
Clearflex H&T FGH B0是一种线性低密度聚乙烯,由专有的增强Z-N催化剂制成,适用于吹膜技术。该树脂含有抗氧化剂,具有非常低的密度和高分子量。与标准Clearflex VLDPE等级相比,Clearflex H&T FGH B0具有较低的密封起始温度、优异的光学性能和机械性能。主要用途Clearflex H&T FGH B0被推荐用于生产要求光学性能、耐穿刺性、冲击强度和良好密封性相结合的吹塑薄膜。Clearflex H&T FGH B0也推荐用于层压膜的生产。 Clearflex H&T FGH B0 is a linear low density polyethylene, made by proprietary enhanced Z-N catalyst, suitable for blown film technology. The resin, containing antioxidants, is characterized by a very low density and high molecular weight. Compared to std Clearflex VLDPE grades, Clearflex H&T FGH B0 offers lower seal initiation temperature, excellent optical properties and mechanical performances. Main Application Clearflex H&T FGH B0 is recommended to produce blown film requiring a combination of optical properties, puncture resistance and impact strength and very good sealability. Clearflex H&T FGH B0 is also recommended in the production of Lamination film. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.911 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
0.90 | g/10min | ISO 1133 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
摩擦系数 friction coefficient |
|||
与自身 - 动态,铸造薄膜 With oneself - dynamic, casting thin films |
> 0.50 | ISO 8295 | |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
10 to 50µm | ||
拉伸模量 Tensile modulus |
ISO 527-3 | ||
1% 正割,MD,铸造薄膜 1% secant, MD, cast thin film |
140 | MPa | ISO 527-3 |
1% 正割,TD,铸造薄膜 1% secant, TD, cast thin film |
MPa | ISO 527-3 | |
拉伸强度 tensile strength |
ISO 527-3 | ||
MD,屈服,吹塑薄膜 MD, yield, blow molded film |
MPa | ISO 527-3 | |
TD,屈服,吹塑薄膜 TD, yield, blow molded film |
MPa | ISO 527-3 | |
MD,断裂,吹塑薄膜 MD, fracture, blow molded film |
MPa | ISO 527-3 | |
TD,断裂,吹塑薄膜 TD, fracture, blow molded film |
MPa | ISO 527-3 | |
拉伸应变 Tensile strain |
ISO 527-3 | ||
MD,断裂,铸造薄膜 MD, fracture, cast thin film |
% | ISO 527-3 | |
TD,断裂,铸造薄膜 TD, fracture, cast thin film |
% | ISO 527-3 | |
落锤冲击 Drop hammer impact 2 |
|||
铸造薄膜 Casting thin film 2 |
g | ISO 7765-1/A | |
撕裂强度 tear strength |
ISO 6383-2 | ||
MD,铸造薄膜 MD, cast thin film |
kN/m | ISO 6383-2 | |
TD,铸造薄膜 TD, cast thin film |
kN/m | ISO 6383-2 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
脆化温度 Embrittlement temperature |
℃ | ASTM D746 | |
维卡软化温度 Vicat Softening Temp |
℃ | ISO 306/A | |
熔融温度 Melting temperature |
℃ | 内部方法 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
|||
45°,铸造薄膜 45 °, cast thin film |
ASTM D2457 | ||
雾度 Haze |
|||
铸造薄膜 Casting thin film |
% | ISO 14782 |
备注 |
---|
2 F50 |
【新闻资讯】查看全部 ![]()
前10月化学原料和制品制造业利润总额同比增长1.16倍
2021-11-29 搜料网资讯: 国家统计局11月27日公布的数据显示,110月份,全国规模以上工业企业实现利润总额71649.9亿元,同比增长42.2%,比2019年110月份增长43.2%,两年平均增长19.7%。其中,化学原料 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |