牌号简介 About |
---|
Clearflex® FF 106是一种含抗氧化剂的己烯共聚物线性低密度聚乙烯(C6-LLDPE),适用于吹塑薄膜挤出。用Clearflex® FF 106制造的薄膜具有高光学性能(雾度、光泽度)、最佳冲击性、撕裂性和耐刺穿性。主要应用Clearflex® FF 106推荐用于低规格农业吹塑拉伸膜的生产,共挤或与低密度聚乙烯共混。由于其优异的气泡稳定性,Clearflex® FF 106是生产需要高机械性能的低规格薄膜的理想选择。 Clearflex FF 106 is a hexene copolymer linear low density polyethylene (C6-LLDPE), with antioxidants, suitable for blown film extrusion. Film manufactured with Clearflex FF 106 are characterised by high optical properties (haze, gloss), optimum impact, tear and puncture resistance. Main Application Clearflex FF 106 is recommended for the production of blown stretch film, low gauge agricultural, in coextrusion or blending with LDPE. Because of its excellent bubble stability, Clearflex FF 106 is the ideal choice for the production of low gauge film where high mechanical properties are required. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.918 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
0.60 | g/10min | ISO 1133 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
摩擦系数 friction coefficient |
|||
与自身 - 动态,吹塑薄膜 Self dynamic, blow molded film |
> 0.50 | ISO 8295 | |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
25 | µm | |
薄膜厚度 film thickness |
10 to 50µm | ||
拉伸模量 Tensile modulus |
ISO 527-3 | ||
1% 正割,MD,25 µm,吹塑薄膜 1% secant, MD, 25 µ m, blow molded film |
MPa | ISO 527-3 | |
1% 正割,TD,25 µm,吹塑薄膜 1% secant, TD, 25 µ m, blow molded film |
MPa | ISO 527-3 | |
拉伸强度 tensile strength |
ISO 527-3 | ||
MD,屈服,25 µm,吹塑薄膜 MD, yield, 25 µ m, blow molded film |
MPa | ISO 527-3 | |
TD,屈服,25 µm,吹塑薄膜 TD, yield, 25 µ m, blow molded film |
MPa | ISO 527-3 | |
拉伸强度 tensile strength |
ISO 527-3 | ||
MD,断裂,25 µm,吹塑薄膜 MD, fracture, 25 µ m, blow molded film |
MPa | ISO 527-3 | |
TD,断裂,25 µm,吹塑薄膜 TD, fracture, 25 µ m, blow molded film |
MPa | ISO 527-3 | |
拉伸应变 Tensile strain |
ISO 527-3 | ||
MD,断裂,25 µm,吹塑薄膜 MD, fracture, 25 µ m, blow molded film |
% | ISO 527-3 | |
TD,断裂,25 µm,吹塑薄膜 TD, fracture, 25 µ m, blow molded film |
% | ISO 527-3 | |
落锤冲击 Drop hammer impact 2 |
|||
25 µm,吹塑薄膜 25 µ m, blow molded film 2 |
g | ISO 7765-1/A | |
埃尔曼多夫抗撕强度 Elmandorf tear strength 3 |
ISO 6383-2 | ||
MD:25.0 µm MD:25.0 µm |
kN/m | ISO 6383-2 | |
TD:25.0 µm TD:25.0 µm |
kN/m | ISO 6383-2 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
脆化温度 Embrittlement temperature |
℃ | ASTM D746 | |
维卡软化温度 Vicat Softening Temp |
℃ | ISO 306/A | |
熔融温度 Melting temperature |
℃ | 内部方法 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
|||
45°,25 µm,吹塑薄膜 45 °, 25 µ m, blow molded film |
ASTM D2457 | ||
雾度 Haze |
|||
25 µm,吹塑薄膜 25 µ m, blow molded film |
% | ISO 14782 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 F50 |
3 Blown Film |
【新闻资讯】查看全部
德媒:中国领跑疫后全球车市
2020-12-20 搜料网资讯: 中国前进,德国后退:根据一项研究 结果,新冠疫情危机结束后中国汽车市 场将最能继续良性发展。 基于可以期待的增长和迄今对新冠 疫情的成功遏制,行业观察家费迪 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |