牌号简介 About |
---|
LNP Thermocomp RF00CSXS化合物LNP Thermocomp RF00CSXS是一种基于尼龙66树脂的含玻璃纤维化合物。这种材料的附加特性包括:热稳定。又名:lnp*Thermocomp*化合物RF-100-12 hs产品再订购名称:rf00csxs lnp Thermocomp rf00csxs化合物lnp*Thermocomp*rf00csxs是一种基于尼龙66树脂的化合物,含有玻璃纤维。这种材料的附加特性包括:热稳定。也称为:lnp*Thermocomp*化合物rf10012hs产品再订购名称:rf00csxs LNP* THERMOCOMP* RF00CSXS is a compound based on Nylon 66 resin containing Glass Fiber. Added features of this material include: Heat Stabilized. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.72 | g/cm³ | ASTM D792, ISO 1183 |
收缩率 Shrinkage rate |
|||
MD:24 hrs MD:24 hrs |
0.30 | % | ASTM D955 |
TD:24 hrs TD:24 hrs |
0.40 | % | ASTM D955 |
TD:24 hrs TD:24 hrs |
0.44 | % | ISO 294-4 |
MD:24 hrs MD:24 hrs |
0.29 | % | ISO 294-4 |
吸水率 Water absorption rate |
|||
24hr,50% RH 24hr,50% RH |
% | ASTM D570 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
|||
-- -- 1 |
MPa | ASTM D638 | |
-- -- |
MPa | ISO 527-1-2 | |
拉伸强度 tensile strength |
|||
屈服 yield |
MPa | ASTM D638 | |
屈服 yield |
MPa | ISO 527-2 | |
断裂 fracture |
MPa | ASTM D638 | |
断裂 fracture |
MPa | ISO 527-2 | |
拉伸应变 Tensile strain |
|||
屈服 yield |
% | ASTM D638 | |
屈服 yield |
% | ISO 527-2 | |
断裂 fracture |
% | ASTM D638 | |
断裂 fracture |
% | ISO 527-2 | |
弯曲模量 Bending modulus |
|||
-- -- |
MPa | ASTM D790 | |
-- -- |
MPa | ISO 178 | |
弯曲强度 bending strength |
|||
-- -- |
MPa | ASTM D790 | |
-- -- |
MPa | ISO 178 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃ 23℃ |
J/m | ASTM D256 | |
23℃ 23℃ 2 |
kJ/m² | ISO 180-1A | |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
|||
23℃ 23℃ |
J/m | ASTM D4812 | |
23℃ 23℃ 3 |
kJ/m² | ISO 180/1U | |
装有测量仪表的落镖冲击 Dart impact equipped with measuring instruments |
|||
23℃,Energy at Peak Load 23℃,Energy at Peak Load |
J | ASTM D3763 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火,3.2 mm 0.45 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
0.45 MPa,未退火,64 mm跨距 0.45 MPa, unannealed, 64 mm span 4 |
℃ | ISO 75-2/Bf | |
1.8 MPa,未退火,3.2 mm 1.8 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
1.8 MPa,未退火,64 mm跨距 1.8 MPa, unannealed, 64 mm span 5 |
℃ | ISO 75-2/Af | |
线性热膨胀系数 Linear coefficient of thermal expansion |
ASTM E831, ISO 11359-2 | ||
MD:-40~40℃ MD:-40~40℃ |
1/℃ | ||
TD:-40~40℃ TD:-40~40℃ |
1/℃ |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 2.0 in/min |
3 0.079 in/min |
4 Break |
5 80*10*4 |
6 80*10*4 mm |
7 2 mm/min |
【新闻资讯】查看全部
pp资料可进步户外产品的使用寿命
2018-06-19 PP材料耐候性较差,通过改性加工可改善它的耐候性能。改性耐候PP材料具有良好的耐候性,能够抗紫外,抗热氧老化,主要应用于家电产品外壳、室外空调机部件、户外用品等。耐候级的PP材料可以大幅度提高产品在户外恶劣气候条件下的使用寿命。 聚赛龙耐候PP材料一览表: |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |