牌号简介 About |
---|
特点:控制重熔率高,分子量分布窄,均聚聚丙烯,逐批稠度,采用特殊的添加剂包装,清洁度高,能在低旦纤维中高速稳定的纺丝加工性能,耐气体褪色性好。推荐用途:高速纺粘法生产无纺布,低旦纤维熔纺,拉菲亚机织物挤出涂层,通用注塑应用。 Characteristics: Control reologhy high melt flow rate narrow molecular weight distribution Homopolymer polypropylene, lot to lot consistency, with special additives package and high cleanness, to get stable spinning processability in low denier fiber at high speed, good gas fading resistant. Recommended for: Fabrication of Non woven fabrics by high speed Spunbond process, melt spinning of low denier fibers, extrusion coating of raffia woven fabrics, general purpose injection molding applications. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
熔体质量流动速率 Melt Flow Rate 2 |
|||
230℃,2.16kg 230℃,2.16kg 2 |
35 | g/10min | ASTM D1238 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength 3 |
|||
屈服,3.20 mm,注塑成型 Yield, 3.20 mm, injection molding 3 |
34.5 | MPa | ASTM D638 |
拉伸应变 Tensile strain 3 |
|||
屈服,3.20 mm,注塑成型 Yield, 3.20 mm, injection molding 3 |
9.8 | % | ASTM D638 |
弯曲模量 Bending modulus 4 |
|||
1% 正割,3.20 mm,注塑成型 1% cut, 3.20 mm, injection molded 4 |
1480 | MPa | ASTM D790-A |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃,3.2mm,注塑成型 23 ℃, 3.2mm, injection molding |
32 | J/m | ASTM D256-A |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 程序 B |
3 类型 1, 2.0 in/min |
4 类型 1, 0.051 in/min |
【新闻资讯】查看全部
大陆集团推出了新的环保表面材料,使汽车内饰更加柔软耐用
2022-06-10 大陆集团开发了一种新的高质量表面材料:Benova Eco Protect。该材料具有使汽车内部更加可持续、耐用和舒适等优点,目前正在德国制造。大陆集团在弗吉尼亚州温彻斯特的美国工厂将进 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |