Vipel K733-B是一种阻燃型间苯二甲酸聚酯树脂,符合ASTM E 84一级标准,添加1.5%三氧化二锑。VIPEL K733系列树脂非常适合用于手工铺层、喷涂和纤维缠绕工艺,其中需要优异的机械性能和温和的耐化学性。优点阻燃Vipel K733-B只需1.5%三氧化二锑即可满足ASTM E 84 I级火焰蔓延要求。通用的宽配方能力允许在许多过程中使用,并优化成本/性能。耐腐蚀Vipel K733对多种化学环境具有温和的耐化学性。请参阅AOC的“耐腐蚀树脂指南”,了解耐腐蚀信息或有关树脂适用于任何特定化学环境的问题,请联系AOC。 Vipel K733-B is a fire retardant isophthalic polyester resin that meets ASTM E 84 Class I with 1.5% antimony trioxide added. Vipel K733 series resins are ideally suited for use in hand lay-up, spray-up and filament winding processes where outstanding mechanical properties and mild chemical resistance are required. BENEFITS Fire Retardant Vipel K733-B requires only 1.5% antimony trioxide to meet ASTM E 84 Class I flame spread requirements. Versatile Wide formulating capabilities allow for use in many processes and for optimization of cost/performance. Corrosion Resistance Vipel K733 provides mild chemical resistance to a number of chemical environments. Refer to AOC's "Corrosion Resistant Resin Guide" for corrosion resistance information or for questions regarding suitability of a resin to any particular chemical environment contact AOC. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
苯乙烯含量 styrene content |
39 | % | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
96.1 | ℃ | ASTM D648 |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
火焰传播 flame propagation |
|||
1.5% Antimony Trioxide 1.5% Antimony Trioxide |
15.0 | ASTM E84 | |
Smoke Developed(1.5% Antimony Trioxide) Smoke Developed(1.5% Antimony Trioxide) |
650 | ASTM E84 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
Gel to Peak Gel to Peak |
6.0 | min | |
放热峰值 exothermic peak |
℃ | ||
触变指数 Thixotropic index 2 |
|||
Uncured Properties Uncured Properties |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
g/cm³ | ||
粘度 viscosity |
|||
布络克菲尔德 RVT,25℃ 25℃,Brookfield RVT |
Pa·s | ||
胶凝时间 Gelation time |
|||
25℃ 25℃ |
min | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
巴氏硬度 Babbitt hardness |
ASTM D2583 | ||
拉伸模量 Tensile modulus |
MPa | ASTM D638 | |
拉伸强度 tensile strength |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ASTM D638 | |
弯曲模量 Bending modulus |
MPa | ASTM D790 | |
弯曲强度 bending strength |
MPa | ASTM D790 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 2/20 rpm |
【新闻资讯】查看全部
无边框+全新home 键 新资料助阵IPHONE7
2016-01-08 果粉们YY已久的“无边框设计”也许有望在IPHONE 7中实现!据悉,IPHONE 7和7 Plus将会放弃全铝制机身外壳设计,为转而采用全新的外壳材料。新材料,可让 IPHONE 7告别白带,实现无边框设计,甚至可能取消或改变home键,还能让机身更为轻薄。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |