牌号简介 About |
---|
符合ISO 1043-1的材料规范:用20%长的玻璃纤维增强聚丙烯共聚物。低排放。纤维与聚丙烯基体发生化学耦合。球团是圆柱形的,通常和嵌入的纤维一样长10毫米。Celstran成型件具有高强度、高刚度、高热变形等优异的力学性能。由于部件中内置了纤维骨架,因此在高温和低温下缺口冲击强度会增加。长纤维增强能显著降低蠕变。模制品的各向同性收缩使翘曲最小化。通过注射成型,可以制造出具有高再现性的复杂零件。应用领域:汽车功能/结构件 Material code according to ISO 1043-1: PP Polypropylene copolymer reinforced with 20 weight percent long glass fibers. Low emission. The fibers are chemically coupled to the polypropylene matrix. The pellets are cylindrical and normally as well as the embedded fibers 10 mm long. Parts molded of CELSTRAN have outstanding mechanical properties such as high strength and stiffness combined with high heat deflection. The notched impact strength is increased at elevated and low temperatures due to the fiber skeleton built in the parts. The long fiber reinforcement reduces creep significantly. The very isotropic shrinkage in the molded parts minimizes the warpage. Complex parts can be manufactured with high reproducibility by injection molding. Application field: Functional/structural parts for automotive |
产品描述 Product Description
厂家:美国塞拉尼斯 Celanese
类别:PP共聚 PP copolymer
用途:汽车领域的应用;
加工条件:注射成型 Injection Molding
性能特点: 机械强度好; 化学耦合; 共聚物; 低VOC; 耐低温冲击; 各向同性好; 低翘曲性; 韧性好; Good Rigidity,Low warping,Good flexibility,Low odor,Chemical coupling,Copolymer,low-temperature impact resistance,Good Isotropy
填料:玻璃纤维 20
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.03 | g/cm³ | ISO 1183 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
4700 | MPa | ISO 527-2/1A |
拉伸强度 tensile strength |
|||
断裂 fracture |
84.0 | MPa | ISO 527-2/1A/5 |
拉伸应变 Tensile strain |
|||
断裂 fracture |
2.5 | % | ISO 527-2/1A/5 |
弯曲模量 Bending modulus |
|||
23℃ 23℃ |
4500 | MPa | |
80℃ 80℃ |
MPa | ||
弯曲强度 bending strength |
|||
23℃ 23℃ |
MPa | ||
80℃ 80℃ |
MPa | ||
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
-30℃ -30℃ |
kJ/m² | ||
23℃ 23℃ |
kJ/m² | ||
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
|||
-30℃ -30℃ |
kJ/m² | ||
23℃ 23℃ |
kJ/m² | ||
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃ 23℃ |
kJ/m² | ISO 180-1A | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A |
备注 | |||
---|---|---|---|
暂无数据 |
【新闻资讯】查看全部
喜报!上海石化新型塑料获工博会新材料奖
2020-09-25 搜料网资讯:日前,在第22届中国国际工业博览会(CIFF)上,上海石化与上海吉虞实业有限公司的新型高韧性聚酯类工程塑料及应用荣获工博会CIIF新材料奖。 新型高韧性聚酯类工程塑 |
喜报!上海石化新型塑料获工博会新材料奖 搜料网资讯:日前,在第22届中国国际工业博览会(CIFF)上,上海石化与上海吉虞实业有限公司的“新型高韧性聚酯类工程塑料及应用”荣获工博会CIIF新材料奖。
新型高韧性聚酯类工程塑料由上海石化开发。通过设计聚酯分子链结构,上海石化使用自主研发的一步法聚酯液相增粘技术,解决了聚酯板材成型过程的关键技术问题,形成聚酯板用基料成熟的工业化连续生产技术,填补国内聚酯板用基料生产技术和产品空白,实现国内首家产业化生产该产品,围绕产品核心技术申请中国发明专利3项。 作为新一代超轻箱包原料,该材料具有超强韧性,抗冲强度是PC工程塑料的1.7倍、ABS树脂的5倍,解决了ABS产品易破裂的问题。与PC、ABS等箱包料相比具有价格优势。板材回收利用率90%以上,每年可减少大量固废。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
价格走势图
开始时间:
结束时间:
材料厂家:
【牌号齐全,内容全面】
全网共2500+项牌号+上游原料单体+原油价格,最长可追溯近20年价格行情
【精准,及时,权威!】
专业团队挖掘行情信息,第一时间发布行情
抱歉!该牌号暂无认证数据。
免责声明:参考价格是搜料网根据网络大数据拟合分析的结果,仅供参考。实际成交价取决但不限于以下因素:下单时间,付款方式,交货方式,数量,税费,色号,产地,项目信息。
抱歉!暂无数据。
抱歉!暂无数据。